Pro-osteogenic stimulation of bone cells by bioactive ceramic-coated orthopedic implants is influenced by both surface roughness and material chemistry; however, their concomitant impact on osteoblast behavior is not well understood. The aim of this study is to investigate the effects of nano-scale roughness and chemistry of bioactive silica-calcium phosphate nanocomposite (SCPC50) coated Ti-6Al-4V on modulating early bone cell responses. Cell attachment was higher on SCPC50-coated substrates compared to the uncoated controls; however, cells on the uncoated substrate exhibited greater spreading and superior quality of F-actin filaments than cells on the SCPC50-coated substrates. The poor F-actin filament organization on SCPC50-coated substrates is thought to be due to the enhanced calcium uptake by the ceramic surface. Dissolution analyses showed that an increase in surface roughness was accompanied by increased calcium uptake, and increased phosphorous and silicon release, all of which appear to interfere with F-actin assembly and osteoblast morphology. Moreover, cell attachment onto the SCPC50-coated substrates correlated with the known adsorption of fibronectin, and was independent of surface roughness. High-throughput genome sequencing showed enhanced expression of extracellular matrix and cell differentiation related genes. These results demonstrate a synergistic relationship between bioactive ceramic coating roughness and material chemistry resulting in a phenotype that leads to early osteoblast differentiation.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1002/jbm.a.35326 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effect of post-processing on the surface, optical, mechanical, and dimensional properties of 3D-printed orthodontic clear retainers.
Clin Oral Investig
January 2025
School of Materials Science and Innovation, Faculty of Science, Mahidol University, Phuttamonthon 4 Road, Salaya, Phuttamonthon District, Nakhon Pathom, 73170, Thailand.
Objectives: To address the high surface roughness and poor optical properties of three-dimensional (3D) printed orthodontic clear retainers, an alternative post-processing protocol was investigated with the goal of achieving improved surface, optical, and mechanical properties while preserving dimensional accuracy.
Materials And Methods: Samples were prepared from two biocompatible methacrylate-based 3D-printing resins (Formlabs Dental LT Clear V2, NextDent OrthoFlex) and one thermoplastic material (Duran). For the 3D-printed resins, one group was post-processed by rinsing in isopropyl alcohol, while another group was centrifuged before post-curing in glycerine.
Droplet-Scale Conversion of Aluminum into Transparent Aluminum Oxide by Low-Voltage Anodization in an Electrowetting System.
Langmuir
January 2025
Information Device Science Laboratory, Division of Materials Science, Nara Institute of Science and Technology, Ikoma City, Nara 630-0192, Japan.
A localized conversion of aluminum into transparent aluminum oxide by droplet-scale anodization is demonstrated in this work. The anodized region can be contained and controlled on the basis of the electrowetting response of the droplet. A highly uniform and transparent anodized spot was achieved using an anodization voltage of 2 V for 10 min.
View Article and Find Full Text PDFStrategy for Fabricating Degradable Low-Surface-Energy Cross-Linked Networks with Excellent Anti-Fouling Properties.
ACS Appl Mater Interfaces
January 2025
National Experimental Teaching Demonstration Center for Materials Science and Engineering, School of Materials Science and Engineering, Beihang University, No. 37 Xueyuan Road, Haidian District, Beijing 100191, China.
Marine biofouling negatively impacts marine industries and ship navigation. However, current coatings are based on a single antifouling mechanism, which is insufficient to cope with the complex and ever-changing marine environment. Herein, multifunctional antifouling coatings were developed using a material system containing perfluoropolyether and caprolactone chains.
View Article and Find Full Text PDFDoes Cigarette Smoke Affect Permanent Resin-Based Crown Materials?
J Esthet Restor Dent
January 2025
Department of Prosthodontic, Faculty of Dentistry, Cukurova University, Adana, Turkey.
Objective: The purpose of this study was to investigate how cigarette smoking affects the surface roughness (R) and stainability of additively and subtractively manufactured resins.
Materials And Methods: Two additively manufactured definitive resins (Dentafab, DF and Formlabs, FL) and a subtractively manufactured resin nanoceramic (Cerasmart, CS) were used to fabricate 60 specimens (14 × 12 × 1 mm). After taking baseline R and color measurements (ΔE), they were divided into two groups (n = 10).
The Influence of Surface Treatment on the Color of Enamel and Dentin: An In Vitro Study Using Machine Learning-Based Analysis.
J Esthet Restor Dent
January 2025
State Key Laboratory of Oral Diseases, National Clinical Research Center for Oral Diseases, Chengdu, China.
Objective: To investigate how surface treatment affects the color of enamel and dentin, and to evaluate whether the color differences are acceptable.
Materials And Methods: Freshly extracted premolars were prepared using diamond burs (blue, red, and yellow tapes). Tooth surfaces were divided into control and acid-etched areas and treated with phosphoric acid (5, 15, 30, 45, and 60 s).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!