Objectives: Tricalcium silicate is the major constituent phase in mineral trioxide aggregate (MTA). It is thus postulated that pure tricalcium silicate can replace the Portland cement component of MTA. The aim of this study was to evaluate bond strength of methacrylate-based (MB) composites, silorane-based (SB) composites, and glass ionomer cement (GIC) to Biodentine® and mineral trioxide aggregate (MTA).
Material And Methods: Acrylic blocks (n=90, 2 mm high, 5 mm diameter central hole) were prepared. In 45 of the samples, the holes were fully filled with Biodentine® and in the other 45 samples, the holes were fully filled with MTA. The Biodentine® and the MTA samples were randomly divided into 3 subgroups of 15 specimens each: Group-1: MB composite; Group-2: SB composite; and Group-3: GIC. For the shear bond strength (SBS) test, each block was secured in a universal testing machine.
Results: The highest (17.7 ± 6.2 MPa) and the lowest (5.8 ± 3.2 MPa) bond strength values were recorded for the MB composite-Biodentine® and the GIC-MTA, respectively. Although the MB composite showed significantly higher bond strength to Biodentine (17.7 ± 6.2) than it did to MTA (8.9 ± 5.7) (p < 0.001), the SB composite (SB and MTA = 7.4 ± 3.3; SB and Biodentine® = 8.0 ± 3,6) and GIC (GIC and MTA = 5.8 ± 3.2; GIC and Biodentine = 6.7 ± 2.6) showed similar bond strength performance with MTA compared with Biodentine (p = 0.73 and p = 0.38, respectively).
Conclusions: The new pure tricalcium-based pulp capping, repair, and endodontic material showed higher shear bond scores compared to MTA when used with the MB composite.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4126826 | PMC |
| http://dx.doi.org/10.1590/1678-775720130660 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Why does silicon have an indirect band gap?
Mater Horiz
January 2025
Department of Materials Science, University of Michigan, Ann Arbor, Michigan 48109, USA.
It is difficult to intuit how electronic structure features-such as band gap magnitude, location of band extrema, effective masses, -arise from the underlying crystal chemistry of a material. Here we present a strategy to distill sparse and chemically-interpretable tight-binding models from density functional theory calculations, enabling us to interpret how multiple orbital interactions in a 3D crystal conspire to shape the overall band structure. Applying this process to silicon, we show that its indirect gap arises from a competition between first and second nearest-neighbor bonds-where second nearest-neighbor interactions pull the conduction band down from Γ to X in a cosine shape, but the first nearest-neighbor bonds push the band up near X, resulting in the characteristic dip of the silicon conduction band.
View Article and Find Full Text PDFCyclic cooperativity contributions determine the hydrogen bond strengths in molecular clusters.
Phys Chem Chem Phys
January 2025
Department of Chemistry, Dr. Harisingh Gour Vishwavidyalaya (A Central University), Sagar-470003, India.
In a recent communication (A. Shivhare, B. Dehariya, S.
View Article and Find Full Text PDFQuantifying the ability of the CFH group as a hydrogen bond donor.
Beilstein J Org Chem
January 2025
Department of Chemistry, University of Rhode Island, 140 Flagg Rd, Kingston, RI 02881, USA.
The CFH group can act as a hydrogen bond donor, serving as a potential surrogate for OH or SH groups but with a weaker hydrogen bond donation ability. Here, we describe a series of CFH group-containing moieties that facilitate hydrogen bond interactions. We survey hydrogen bond donation ability using several established methods, including H NMR-based hydrogen bond acidity determination, UV-vis spectroscopy titration with Reichardt's dye, and H NMR titration using tri--butylphosphine oxide as a hydrogen bond acceptor.
View Article and Find Full Text PDFPhotochemically Activated Microbubble Emulsion, Nd: Yap Laser, and Cerium Oxide Nanoparticles as Canal Disinfectants on Push-Out Bond Strength of Sealer to Root Dentin, Smear Layer, and Antibacterial Efficacy.
Microsc Res Tech
January 2025
Department of Restorative and Prosthetic Dental Sciences, College of Dentistry, Dar Al Uloom University, Riyadh, Saudi Arabia.
Effect of different root canal irrigation regimes microbubble emulsion (MBE) via riboflavin photosensitizer (RFP), cerium oxide (CeO) nanoparticles (NPs), and Nd: YAP laser on antibacterial efficiency, microhardness (MH), smear layer (SL) removal efficacy, and push-out bond strength (PBS) of AH plus sealer to canal dentin. Sixty single-rooted teeth were selected, disinfected, and categorized into four groups based on the type of disinfection. Following disinfection, a pair of samples were randomly selected and visualized under scanning electron microscope (SEM) for SL evaluation.
View Article and Find Full Text PDFCyclo-N : a Novel 5/6 Fused Polynitrogen Anion for High Energy Density Materials.
Adv Sci (Weinh)
January 2025
School of Chemistry and Chemical Engineering, Nanjing University of Science and Technology, Nanjing, Jiangsu, 210094, China.
After cyclo-pentazolate anion, a 5/6 fused structure of N is constructed, and four novel nitrogen-rich ionic compounds are assembled on its basis. The results of the quantum calculations revealed an uneven distribution of electrons on cyclo-N , with significant charge density near the N5/N9 atoms and an ADCH charge of -0.425.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!