AI Article Synopsis
Article Abstract
This study evaluated the influence of silane heat treatment and glass fiber fabrication type, industrially treated (I) or pure (P), on flexural and compressive strength of methacrylate resin bars (BISGMA/TEGDMA, 50/50%). Six groups (n = 10) were created: I-sil: I/silanated; P-sil: P-silanated; I-sil/heat: I/silanated heated to 100°; P-sil/heat: P/silanated heated to 100°; (I: I/not silanated; and P: P/not silanated. Specimens were prepared for flexural strength (10 × 2 × 1 mm) and for compressive strength 9.5 × 5.5 × 3 mm) and tested at 0.5 mm/min. Statistical analysis demonstrated the following for flexural strength (P < 0.05): I-sil: 155.89 ± 45.27(BC); P-sil: 155.89 ± 45.27(BC); I-sil/heat: 130.20 ± 22.11(C); P-sil/heat: 169.86 ± 50.29(AB); I: 131.87 ± 15.86(C). For compressive strength, the following are demonstrated: I-sil: 1367.25 ± 188.77(ab); P-sil: 867.61 ± 102.76(d); I-sil/heat: 1162.98 ± 222.07(c); P-sil/heat: 1499.35 ± 339.06(a); and I: 1245.78 ± 211.16(bc). Due to the impossibility of incorporating the stipulated amount of fiber, P group was excluded. Glass fiber treatment with heated silane enhanced flexural and compressive strength of a reinforced dental methacrylate.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4055137 | PMC |
| http://dx.doi.org/10.1155/2014/364398 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Enoki-Inspired Microfibers and Extracellular Matrix Enhance Biaxially Interlocking Interfaces.
Small Struct
November 2024
Department of Surgery-Transplant and Mary & Dick Holland Regenerative Medicine Program, University of Nebraska Medical Center, Omaha, NE, 68198, USA.
Taking inspiration from diverse interlocking and adhesion structures found in nature, a biaxially interlocking interface is developed in this work. This interface is formed by interconnecting two electrostatically flocked substrates and its mechanical strength is enhanced through the incorporation of enoki mushroom-shaped microfibers and deposited extracellular matrix (ECM). Tips of flocked straight fibers can be transformed into mushroom shapes through thermal treatment.
View Article and Find Full Text PDFHigh early strength concrete incorporating waste derived nanomaterials for sustainable construction.
Sci Rep
December 2024
Department of Civil Engineering, National Research Centre, Dokki, Egypt.
This paper contributes to the expanding knowledge base on nanomaterial-enhanced cementitious composites, offering valuable insights for developing high-performance, sustainable concrete solutions. The study assessed the effects of three different types of nanomaterials-nano clay (NC), nano silica (NS), and nano cellulose (NCel)-on the compressive strength of high-early-strength concrete (HESC) through both experimental studies and a 2 factorial design. Incorporating nanomaterials into the HESC matrix led to a decrease in workability, with NCel demonstrating the least impact on this property across all studied replacement percentages.
View Article and Find Full Text PDFIn this project, cement-based composites reinforced with slag powder (abbreviated as SP), steel slag powder (abbreviated as SSP), and desulfurization gypsum (abbreviated as FGD) were used as the research objects, and the preparation, mechanical properties, and strengthening mechanism of the composites were systematically studied. A laser particle analyzer (Malvern Instruments Analysis) was used to determine that the particle sizes of the raw SSP, SP, and FGD materials were concentrated between 5 and 40 μm, indicating that they were fine-grained minerals. SSP and SP are highly active alkaline substances.
View Article and Find Full Text PDFMechano-Graded Contact-Electrification Interfaces Based Artificial Mechanoreceptors for Robotic Adaptive Reception.
ACS Nano
December 2024
Institute of Functional Nano and Soft Materials (FUNSOM), Joint International Research Laboratory of Carbon-Based Functional Materials and Devices, Soochow University, Suzhou 215123, P. R. China.
Triboelectrification-based artificial mechanoreceptors (TBAMs) is able to convert mechanical stimuli directly into electrical signals, realizing self-adaptive protection and human-machine interactions of robots. However, traditional contact-electrification interfaces are prone to reaching their deformation limits under large pressures, resulting in a relatively narrow linear range. In this work, we fabricated mechano-graded microstructures to modulate the strain behavior of contact-electrification interfaces, simultaneously endowing the TBAMs with a high sensitivity and a wide linear detection range.
View Article and Find Full Text PDFpH-responsive antibacterial emulsion gel based on cinnamaldehyde and carboxymethyl chitosan for fruits preservation applications.
Int J Biol Macromol
December 2024
School of Chemistry and Chemical Engineering, Yantai University, Shandong Province, 264005, China. Electronic address:
Although the natural antibacterial agent, cinnamaldehyde, has been extensively studied in the field of food packaging, its water solubility and instability limit its further applications. The controllable responsive release can be achieved through encapsulation in responsive emulsion systems based on carboxymethyl chitosan. Herein, a pH-responsive antibacterial emulsion gel was constructed from cinnamaldehyde-loaded oil-in-water emulsion templates.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!