An in vitro evaluation of effect of eugenol exposure time on the shear bond strength of two-step and one-step self-etching adhesives to dentin.

Objectives: To evaluate the effect of the eugenol exposure time of an eugenol-based provisional restorative material on the shear bond strength of two-step and one-step self-etching adhesives to dentin, at three different time intervals of 24 h, 7 days, and 14 days.

Materials And Methods: Forty extracted human posterior teeth were sectioned mesiodistally to obtain two halves and the resulting 80 halves were randomly assigned into four groups of 20 specimens each (Group-I, -II, -III, and -IV). Cavities of specified dimensions were prepared to expose dentin surface. In Group-I, temporarization was carried out with noneugenol cement (Orafil-G) for 24 h (control group). In Group-II, -III, and -IV, temporarization was carried out with eugenol cement (intermediate restorative material (IRM)) for 24 h, 7 days, and 14 days, respectively. Each group was further divided into two subgroups of 10 teeth each for two-step (Adper SE Plus) and one-step (Adper Easy One) self-etch adhesive systems, respectively. A plastic tube loaded with microhybrid composite resin (Filtek Z-350, 3M) was placed over the dentin surface and light cured. The specimens were subjected to shear stress in universal testing machine.

Results: Group-II yielded low shear bond strength values compared with Group-III, -IV, and Group-I, which was statistically significant.

Conclusions: The prior use of eugenol containing temporary restorative material reduced the bond strength of self-etch adhesive systems at 24-h period. No reduction in bond strength at 7 or 14 days exposure was observed with either two-step or one-step self-etch adhesive.