Fracture resistance of teeth restored with direct and indirect composite restorations.

Objective: Tooth fracture is a common dental problem. By extension of cavity dimensions, the remaining tooth structure weakens and occlusal forces may cause tooth fracture. The aim of this study was to evaluate and compare the fracture resistance of teeth restored with direct and indirect composite restorations.

Materials And Methods: Sixty-five sound maxillary premolar teeth were chosen and randomly divided into five groups each comprising thirteen. Fifty-two teeth received mesio-occluso-distal (MOD) cavities with 4.5mm bucco-lingual width, 4mm pulpal depth and 3mm gingival depth and were divided into the following four groups. G-1: restored with direct composite (Z-250, 3M/ESPE) with cusp coverage, G-2: restored with direct composite (Z-250) without cusp coverage, G-3: restored with direct composite (Gradia, GC-international) with cusp coverage, G-4: restored with indirect composite (Gradia, GC-International) with cusp coverage. Intact teeth were used in G-5 as control. The teeth were subjected to a compressive axial loading using a 4 mm diameter rod in a universal testing machine with 1 mm/min speed. Data were analyzed using one-way ANOVA and Tukey tests.

Results: THE MEAN FRACTURE STRENGTH RECORDED WAS: G-1: 1148.46N±262, G-2: 791.54N±235, G-3: 880.00N±123, G-4: 800.00N±187, G-5: 1051.54N±345. ANOVA revealed significant differences between groups (p<0.05). Tukey test showed significant difference between group 1 and the other groups. There was no significant difference among other groups.

Conclusion: Direct composite (Z-250) with cusp coverage is a desirable treatment for weakened teeth. Treatment with Z-250 without cusp coverage, direct and indirect Gradia with cusp coverage restored the strength of the teeth to the level of intact teeth.