Graphene nanosheets (GNS) were used as anodes in full Li-ion cells and LiFePO4 (LFPO) was used as the cathode. A rapid decrease in capacity was observed following the first cycle, the origin of which was assigned to Li consumption in the solid-electrolyte interface (SEI) formation. A reduction of the irreversible capacity from 120 to a value as low as 20 mAh g(-1), similar to a commercial graphite anode, was possible through a prelithiation treatment prior to cell assembling. However, the GNS electrode barely delivered a capacity ca. 40 mAh g(-1) at the end of cycle 50, notably lower than that of the graphite electrode (ca. 100 mAh g(-1)). X-ray photoelectron spectroscopy spectra of the pristine electrodes at the end of 6th and 22nd charges, combined with depth profile analysis, supplied valuable information on the thickness and composition of the SEI. The spectra revealed that the SEI formed on the graphite electrode was much thicker than that formed on the GNS electrode and that its composition was controlled mainly by Li2CO3. The strength and the stability of Li2CO3 are two requisites for establishing a good SEI, which is the reason why the cell made from graphite performed better.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1021/am405197s | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Ternary NASICON-Type NaVMnFe(PO)/NC@CNTs Cathode with Reversible Multielectron Reaction and Long Life for Na-Ion Batteries.
ACS Appl Mater Interfaces
January 2025
Key Laboratory of Low Carbon Energy and Chemical Engineering of Gansu Province, Lanzhou 730050, China.
Na superionic conductor (NASICON)-structure NaMnV(PO) (NVMP) electrode materials reveal highly attractive application prospects due to ultrahigh energy density originating from two-electron reactions. Nevertheless, NVMP also encounters challenges with its poor electronic conductivity, Mn dissolution, and Jahn-Teller distortion. To address this issue, utilizing N-doped carbon layers and carbon nanotubes (CNTs) for dual encapsulation enhances the material's electronic conductivity, creating an effective electron transport network that promotes the rapid diffusion and storage of Na.
View Article and Find Full Text PDFUltrafast Preparation of High-Entropy NASICON Cathode Enables Stabilized Multielectron Redox and Wide-Temperature (-50-60 °C) Workability in Sodium-Ion Batteries.
Adv Mater
January 2025
MOE Key Laboratory for UV Light-Emitting Materials and Technology, Department of Physics, Northeast Normal University, Changchun, 130024, P. R. China.
Avoiding severe structural distortion, irreversible phase transition, and realizing the stabilized multielectron redox are vital for promoting the development of high-performance NASICON-type cathode materials for sodium-ion batteries (SIBs). Herein, a high-entropy NaVFeTiMnCr(PO) (HE-NaTMP) cathode material is prepared by ultrafast high-temperature shock, which inhibits the possibility of phase separation and achieves reversible and stable multielectron transfer of 2.4/2.
View Article and Find Full Text PDFTwo Steps Li Ion Storage Mechanism in Ruddlesden-Popper LiLaTiO.
Adv Sci (Weinh)
January 2025
Emerging Materials R&D Division, Korea Institute of Ceramic Engineering & Technology, Jinju, Gyeongnam, 52851, Republic of Korea.
Innovative anode materials are essential for achieving high-energy-density lithium-ion batteries (LIBs) with longer lifetimes. Thus far, only a few studies have explored the use of layered perovskite structures as LIB anode materials. In this study, the study demonstrates the performance and charge/discharge mechanism of the previously undefined Ruddlesden-Popper Li₂La₂Ti₃O₁₀ (RPLLTO) as an anode material for LIBs.
View Article and Find Full Text PDFBinary Metal Alloy Electrocatalyst Synergistically Accelerates the Bidirectional Polysulfide Conversions in Lithium-Sulfur Batteries.
Nano Lett
January 2025
State Key Laboratory of Coordination Chemistry, MOE Key Laboratory of Mesoscopic Chemistry, MOE Key Laboratory of High Performance Polymer Materials and Technology, MOE Engineering Research Center of Photoresist Materials, Jiangsu Key Laboratory of Advanced Organic Materials, Tianchang New Materials and Energy Technology Research Center, Institute of Green Chemistry and Engineering, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210023, China.
The sluggish redox kinetics of polysulfides and the resulting shuttle effect remain significant challenges for the practical utilization of lithium-sulfur (Li-S) batteries. To address the unidirectional catalytic limitations of conventional electrocatalysts, we herein report a binary metal (CoNi) alloy embedded in a carbon matrix on carbon nanofibers (CoNi@C-CNFs) as a highly efficient electrocatalyst to accelerate bidirectional polysulfide conversions. Time-of-flight secondary ion mass spectrometry (TOF-SIMS) reveals a significantly improved catalytic effect of the CoNi alloy toward polysulfide conversions after introducing the Ni component.
View Article and Find Full Text PDFConstruction of Low-Crystallinity Three-Dimensional Flower-like Cobalt-Doped Nickel Hydroxide for High-Performance Nickel-Zinc Batteries.
ACS Appl Mater Interfaces
January 2025
School of Chemistry, South China Normal University, Guangzhou 510006, People's Republic of China.
The main limitations of aqueous nickel-zinc batteries are their relatively low energy density and short cycle life, which are inextricably linked to the limitations of nickel-based cathodes. In this study, a low-crystallinity flower-like cobalt-doped nickel hydroxide (α-Ni(OH)-0.2Co) is constructed by hydrothermal reaction and employed as high-energy-density cathode for aqueous rechargeable nickel-zinc batteries.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!