Objectives: To compare in-vitro micro-shear bond strengths (μSBS) of resin composite to calcium silicate cement (Biodentine™) vs. glass ionomer cement vs. resin modified glass ionomer cement (RM-GIC) using an adhesive in self-etch (SE)/total etch (TE) mode after aging three substrates and bond and characterizing their failure modes.
Methods: Resin composite was SE/TE bonded to 920 standardized disks of Biodentine™, GIC & RM-GIC. Dividing samples into two groups, the first underwent early (t=0min, 5min, 20min, 24h) or delayed (t=2wk, 1 month, 3 months, 6 months) substrate aging before bonding and μSBS (t=24h) testing. In the second, adhesive was applied after either early (t=5min) or delayed (t=2wk) substrate aging and then tested after bond aging (t=2wk, 1 month, 3 months, 6 months). The failure modes were identified using stereomicroscope. SEM images of selected samples were analyzed.
Results: No significant differences were observed between (SE)/(TE) bonding modes (P=0.42). With substrate aging, a significant reduction in μSBS occurred between early and delayed time intervals for Biodentine™ (P=0.001), but none for the GIC/RM-GIC (P=0.465, P=0.512 respectively). With bond aging, there was no significant difference between time intervals for all groups, except at 6 months for the GIC (P<0.05). Modes of failure were primarily cohesive within all the substrates (68.82%) followed by adhesive failure at the resin-substrate interface (21.71%).
Significance: Biodentine™ is a weak restorative material in its early setting phase. Placing the overlying resin composite as part of the laminate/layered definitive restoration is best delayed for >2wk to allow sufficient intrinsic maturation to withstand contraction forces from the resin composite. A total-etch or self-etch adhesive may be used.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2013.12.010 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The impact of bleaching using 15% carbamide peroxide on surface properties of CAD-CAM composite structures.
Sci Rep
January 2025
Division of Dentistry, School of Medical Sciences, The University of Manchester, Manchester, M13 9PL, UK.
This study aims to evaluate the effects of the home bleaching method on the surface microhardness and surface roughness of both polished and unpolished CAD-CAM resin composite materials. A polymer-infiltrated ceramic network (PICN) block, Enamic (VE), along with four resin composite blocks (RCB) (Grandio [GN], Lava™ Ultimate [LV], BRILLIANT Crios [B], and Cerasmart [CS]), were prepared to dimensions of 14 mm × 12 mm × 2 mm and were categorized into unpolished and polished groups (n = 4). Microhardness measurements were conducted using a Vickers microhardness tester (300 gf load for 20 s) at various time points: before home bleaching, after home bleaching with 15% Opalescence for 8 h and for 56 h, 24 h after bleaching, and one month after bleaching.
View Article and Find Full Text PDFMeasurement of Fluoride Ion Release From Restorative Material Using an Ion-Selective Electrode and Ultraviolet-Visible Light Spectrophotometer.
J Int Soc Prev Community Dent
December 2024
Department of Environmental Science, School of Life Sciences, Mysuru, JSS Academy of Higher Education and Research, Mysore, Karnataka, India.
Background: Importance of fluoride in dental restorative materials for preventing secondary caries. Several commercially available tooth-colored dental restorative materials, such as glass ionomer cement, resin composites, and compomers were used for this study.
Aim: To evaluate the amount of fluoride release from tooth-colored restorative materials [Conventional Glass Ionomer Cement (GC Fuji II)], Resin-modified Glass Ionomer Cement (ACTIVA BioACTIVE-RESTORATIVE), and Giomer (BEAUTIFIL II LS)] using ion-selective electrode (ISE) and spectrophotometer using zirconyl alizarin red dye method.
Different Composite Veneer Surface Preparations for Metal Orthodontic Bracket Bonding: An In Vitro Study.
Int J Dent
January 2025
Department of Orthodontics, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran.
This research aimed to assess the shear bond strength (SBS) of metal brackets bonded to composite veneers using different surface preparations. One-hundred composite disks were divided into 10 different groups whereby each group combines a surface preparation (roughening or no roughening), etching agent (37% phosphoric or 9.5% hydrofluoric acid), adhesive protocol (self-etch or total-etch), and bonding agent (with or without G-Premio Bond).
View Article and Find Full Text PDFGrey Forecasting for technoeconomic sustainability of fiberglass composite waste recycling in developing countries.
Heliyon
January 2025
Department of Architecture and Built Environment, University of Nottingham, NG7 2RD, UK.
The demand for engineered composites particularly fiberglass reinforced polymers (FRP) is gaining momentum. The manufacturing of virgin input-resins for these composites involves the use of certain materials which poses serious environmental implication. This study has exclusively applied and investigated the Grey Forecasting model for management of FRP waste in developing countries to minimize the virgin inputs and likely environmental impacts.
View Article and Find Full Text PDFMinimally Invasive Fixed Prosthodontics: A Narrative Review.
J Esthet Restor Dent
January 2025
Department of Prosthodontics, Tufts University School of Dental Medicine, Boston, Massachusetts, USA.
Objective: Minimally invasive dentistry is being widely practiced. The center stone is to be as conservative as possible to minimize unnecessary removal of healthy tooth structure. In prosthodontics the patients have generalized and combined nature of diseases.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!