Objective: The aim of this study was to determine the erbium-doped yttrium aluminum garnet (Er:YAG) laser transmission ratio through different dental ceramics with different thicknesses.
Background Data: Laser debonding procedure of adhesively luted all-ceramic restorations is based on the transmission of laser energy through the ceramic and the ablation of resin cement, because of the transmitted laser energy.
Methods: Five different dental ceramics were evaluated in this study: sintered zirconium-oxide core ceramic, monolithic zirconium-oxide ceramic, feldspathic ceramic, leucite-reinforced glass ceramic, and lithium disilicate-reinforced glass ceramic. Two ceramic discs with different thicknesses (0.5 and 1 mm) were fabricated for each group. Ceramic discs were placed between the sensor membrane of the laser power meter and the tip of the contact handpiece of an Er:YAG laser device with the aid of a custom- made acrylic holder. The transmission ratio of Er:YAG laser energy (500 mJ, 2 Hz, 1 W, 1000 μs) through different ceramic discs was measured with the power meter. Ten measurements were made for each group and the results were analyzed with two way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests.
Results: The highest transmission ratio was determined for lithium disilicate-reinforced ceramic with 0.5 mm thickness (88%) and the lowest was determined for feldspathic ceramic with 1 mm thickness (44%). The differences among the different ceramics and between the different thicknesses were significant (p<0.05).
Conclusions: Ceramic type and thickness should be taken into consideration to adjust the laser irradiation parameters during laser debonding of adhesively luted all-ceramic restorations.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1089/pho.2013.3611 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Enhanced vertical bone augmentation in rat parietal bone using hydroxyapatite-coated polytetrafluoroethylene domes with Erbium Yttrium Aluminum Garnet pulsed laser deposition.
J Prosthodont Res
January 2025
Department of Orthodontics, Osaka Dental University, Hirakata, Japan.
Purpose: To perform vertical bone augmentation on rat parietal bone by coating the inner surface of dense polytetrafluoroethylene (d-PTFE) domes with hydroxyapatite (HA) using Erbium Yttrium Aluminum Garnet (Er:YAG) pulsed laser deposition in a rat model.
Methods: The d-PTFE plate surface, α-tricalcium phosphate (α-TCP) coating, and HA coating were measured using scanning electron microscopy and X-ray diffraction to confirm the replacement of α-TCP with HA via high-pressure steam sterilization. The dome was glued to the center of the rat parietal bone and closed with periosteal and epithelial sutures.
Effect of different surface conditioning methods and low pH solutions on the shear bond strength of orthodontic brackets to newly introduced CAD/CAM materials.
Heliyon
November 2024
Department of Orthodontics, Faculty of Dentistry, University of Health Sciences, Turkey.
Aim: To evaluate the shear bond strength (SBS) of ceramic and metallic orthodontic brackets bonded to lithium disilicate ceramics or hybrid ceramics and subjected to different surface conditioning treatments.
Materials And Methods: In total, 300 specimens were fabricated from GC LiSi (lithium disilicate) and GC Cerasmart (hybrid) ceramic blocks. The specimens were divided into four groups according to the following surface treatments: hydrofluoric acid (HF); sandblasting with 50 μm aluminum oxide; Monobond Etch and Prime; and erbium-doped yttrium aluminum garnet (Er-YAG) laser.
Dentinal Tubule Occluding Efficacy Of Er: YAG Laser And Universal Adhesive Loaded With Nano-Carbonated Apatite.
Braz Dent J
July 2024
Conservative Dentistry Department, Faculty of Dentistry, Cairo University, Egypt. Postal Code: 11553.
ER:YAG laser and experimental resin-based dental adhesive loaded with functionalized carbonated apatite filler were used in this study to evaluate the dentin interaction in terms of penetration and occlusion of the dentinal tubules aiding in the control of dentin hypersensitivity (DH). Spheroidal Carbonated apatite nanoparticles (N-CAP), with an average size of 20±5 nm diameter, were synthesized, characterized, and incorporated in a universal adhesive "All Bond Universal, Bisco, USA", in (2% weight) concentration. Er:YAG laser "Lightwalker, FOTONA, EU" was adjusted to an energy output of 40mJ/ pulse and pulse repetition of 10 Hz for 10 seconds.
View Article and Find Full Text PDFRoot surface roughness evaluation following application of different periodontal instruments and Er:YAG laser: A profilometry and SEM study.
Lasers Med Sci
April 2024
Department of Periodontology, Hamidiye Dental Faculty, University of Health Sciences, Istanbul, Turkey.
Aim: The aim of the present study was to evaluate the efficacy of 30-angled Er:YAG laser tip and different periodontal instruments on root surface roughness and morphology in vitro.
Methods: Eighteen bovine teeth root without carious lesion were decoronated from the cementoenamel junction and seperated longitidunally. A total of 36 obtained blocks were mounted in resin blocks and polished with silicon carbide papers under water irrigation.
Use of Phototherapy and Er-YAG Laser in the Management of Mandible Osteoradionecrosis: A Case Report.
J Lasers Med Sci
November 2023
School of Dentistry, University of São Paulo, São Paulo, São Paulo, Brazil.
Article Synopsis
- * Following her diagnosis, she had multiple dental extractions that led to bone exposure and complications, which were treated with photobiomodulation therapy and antimicrobial photodynamic therapy, resulting in improved clinical conditions.
- * After removing necrotic bone with a specialized laser, the patient successfully received dental prosthetics and is currently being monitored, showing no signs of recurrence, indicating potential effectiveness of laser treatments for ORN.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!