Purpose: To evaluate the influence of heat treatment (HT) procedures of a pre-hydrolyzed silane on bond strength of resin cement to a feldspathic ceramic.
Materials And Methods: Ceramic and composite blocks (N = 30) were divided into six groups (n = 5) and subjected to the following conditioning procedures: G1: 9.6% hydrofluoric acid (HF) for 20 s + silane (RelyX Ceramic Primer, 3M ESPE) + resin cement (Panavia F2.0, Kuraray) (control); G2: HF (20 s) + silane + heat treatment in furnace (HTF) (100°C, 2 min) + resin cement; G3: silane + HTF + resin cement; G4- HF (20 s) + silane + heat treatment with hot air (HTA) (50 ± 5°C for 1 min) + resin cement; G5: silane + HTA + resin cement; G6: silane + resin cement. The microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using a stereomicroscope and SEM to categorize the failure types. The data were statistically evaluated using one-way ANOVA and Tukey's test (5%).
Results: The control group (G1) showed no pre-test failures and presented significantly higher mean MTBS (16.01 ± 1.12 MPa) than did other groups (2.63 ± 1.05 to 12.55 ± 1.52 MPa) (p = 0.0001). In the groups where HF was not used, HTF (G3: 12.55 ± 1.52 MPa) showed significantly higher MTBS than did HTA (G5: 2.63 ± 1.05 MPa) (p < 0.05). All failure types were mixed, ie, adhesive between the resin cement and ceramic accompanied by cohesive failure in the cement.
Conclusion: Heat treatment procedures for the pre-hydrolyzed silane either in a furnace or with the application of hot air cannot replace the use of HF gel for the adhesion of resin cement to feldspathic ceramic. Yet when mean bond strengths and incidence of pre-test failures are considered, furnace heat treatment delivered the second best results after the control group, being considerably better than hot air application.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.a30896 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Colophony in Dentistry: Routes of Exposure and Reported Reactions.
Dermatitis
January 2025
Department of Dermatology, Park Nicollet Contact Dermatitis Clinic, Minneapolis, Minnesota, USA.
Colophony is a solid form of resin derived from coniferous trees that has both adhesive and water-resistant properties. For these reasons, this allergen is incorporated into many personal care products, medications, and occupational materials, and is thus commonly implicated in allergic contact dermatitis. Dedicated "dental" allergen series often include colophony, but dermatologists are likely not well-versed on its use in a dental setting.
View Article and Find Full Text PDFEvaluation of the effect of different irrigation solutions used in regenerative endodontic treatment of necrotic molar teeth with open apex on postoperative pain- randomized clinical trial.
Clin Oral Investig
January 2025
Department of Pedodontics, Faculty of Dentistry, Erciyes University, 38039, Kayseri, Türkiye.
Objectives: This study evaluates the effect of different irrigation solutions for postoperative pain in the regenerative endodontic treatments (RET) of necrotic teeth with open apex.
Materials And Methods: This study included necrotic, deeply carious lower molars of 42 patients. Access cavities of the teeth were opened and working lengths were measured at the first visit.
Impact of surface pre-treatment on bond strength between cement and zirconia: A systematic review and network meta-analysis.
J Prosthet Dent
January 2025
Associate Professor, Department of Prosthodontics, Dental Branch, Islamic Azad University of Medical Sciences, Tehran, Iran.
Statement Of Problem: The optimal zirconia pretreatment, contingent upon the type of cement used, warrants further research.
Purpose: The purpose of this investigation was to evaluate the influence of various surface pretreatments on the bonding efficacy of cement to zirconia.
Material And Methods: A comprehensive search was conducted across the PubMed, Embase, Scopus, and Web of Science databases for in vitro studies related to bonding with zirconia up to April 2024, supplemented by a manual search.
Bond strength to eroded dentin as per chlorhexidine use for controlling erosive wear or interface aging: an 18-month assay.
Braz Oral Res
January 2025
Universidade de São Paulo - USP, School of Dentistry, Department of Operative Dentistry, São Paulo, SP, Brazil.
The aim of this study was to assess the effect of a chlorhexidine digluconate solution (CHX) applied as an antiproteolytic agent for controlling erosive tooth wear or as part of the adhesive treatment on long-term bond strength to eroded dentin. Dentin specimens were abraded with a 600-grit silicon carbide (SiC) paper for 1 min (sound dentin - S), subsequently treated with 2% CHX for 1 min (with excess removed, followed by a 6-hour rest), and eroded by exposure to Coca-Cola for 5 min, three times a day, for 5 days (CHX-treated and eroded dentin - CHXE), or only eroded (eroded dentin - E). The specimens were acid-etched (15 s), rinsed (30 s), dried (15 s), and rehydrated with 1.
View Article and Find Full Text PDFNovel triangle papilla access approach for interdental bone defect regeneration: A case study.
Clin Adv Periodontics
January 2025
Department of Dentistry and Oral Surgery, Keio University School of Medicine, Tokyo, Japan.
Background: Successful periodontal regeneration depends on primary wound closure and interdental papilla preservation. In this case study, we introduce a novel triangle papilla access approach (T-PAA) performed under a surgical microscope for treating interdental bone defects. In this novel approach, buccal incisions were used to access root surfaces and bone defects, avoiding interdental papilla incisions and preventing papillary collapse and necrosis.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!