Photopolymerizable phosphate acrylates as comonomers in dental adhesives with or without triclosan monomer units.

Phosphate diacrylates (CO-DAP, TMP-DAP) based on castor oil or trimethylolpropane were synthesized and evaluated in dental adhesive formulations in comparison with 3-acryloyloxy-2-hydroxypropyl methacrylate phosphate (AMP-P). In an attempt to promote antibacterial activity, another photopolymerizable monomer (TCS-UMA) containing 5-chloro-2-(2,4-dichlorophenoxy)phenol moiety (triclosan) was prepared and incorporated in adhesive resins. Each of these monomers had a molecular structure confirmed by spectral methods. The photopolymerization rates for monomers (0.063-0.088s(-1)) were lower than those determined in the monomer combinations (0.116-0.158s(-1)) incorporating phosphate diacrylate (11wt.%), BisGMA (33wt.%), TEGDMA (10wt.%), UDMA (10wt.%) and HEMA (15wt.%), the degree of conversion varying between 63.4 and 74.5%. The formed copolymers showed high values for water sorption (18.65-57.02μg/mm(3)) and water solubility (3.51-13.38μg/mm(3)), and the contact angle was dependent on the presence of CO-DAP (θF1: 66.67°), TMP-DAP (θF2: 55.05°) or AMP-P (θF3: 52.90°) in the photocrosslinked specimens compared to the sample without phosphate monomer (θF4: 82.14°). The scanning electron microscopy image of the dentin-resin composite interface after applying our F1 formulation (pH: 4.1) and its light-curing for 20s supports the evidence of the formation of the hybrid layer with the tooth structure created by self-etching approach, with no gaps or cracks in the adhesive. A comparative analysis of the adhesion achieved with commercial adhesive systems (Single Bond Universal, C-Bond) rather indicates similarities than differences between them. The addition of triclosan methacrylate (1wt.%) into the formulation inhibited the bacterial growth of the Streptococcus mutans and Escherichia coli in the direct contact area due to the covalently linked antibacterial monomer.