Aim: This in vitro study was designed to investigate the effects of daily fluoride exposures on fluoride release and recharge by prereacted glass ionomer (PRG) composite and nano-ionomeric glass ionomer.
Materials And Methods: Seventy-two specimens (36 of each material) were prepared and by placing the restorative materials into Teflon mold. Each specimen was subjected to one of three daily treatments (n = 12): (1) No fluoride treatment (control); (2) application of a fluoride dentifrice (1,000 ppm) once daily; and (3) the same regimen as (2), plus immersion in a 0.05% sodium fluoride (NaF) mouth rinse (225 ppm) immediately following the dentifrice application. Specimens were suspended in a storage vial containing 10 ml demineralizing solution for 6 h and transferred to a new test tube containing 10 ml remineralizing solution for 18 h. Fluoride treatments of the specimens were completed every day prior to their immersion in the demineralizing solution. Media solutions were buffered with equal volumes of total ionic strength adjustment buffer (TISAB) II; fluoride levels were measured using a digital ion analyzer and fluoride electrode throughout the 21 day duration of the experiment.
Results: Nano-ionomeric glass ionomer showed a better amount of fluoride release than PRG composite irrespective of the fluoride treatment supplementation (P < 0.01). Additional fluoride supplementation improved fluoride release and recharge ability for both the materials when compared to their respective control groups. The fluoride recharge for both materials did not show any sustained pattern of release.
Conclusion: Nano-ionomeric glass ionomer demonstrated a greater ability to release and recharge compared with that of PRG composite.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4103/0970-4388.121820 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Calcium Carbonate from Anadara granosa Shells Stimulates FGF2, TGF-β1, and Collagen Type 1 Expression in Rat Dental Pulp.
Eur J Dent
December 2024
Postgraduate Program of Conservative Dentistry Specialist, Faculty of Dental Medicine, Universitas Airlangga, Surabaya, Indonesia.
Objectives: Calcium carbonate (CaCO), a major inorganic component in bones and teeth, offers potential protection against demineralization. This study investigates the effect of CaCO from shells on the expression of fibroblast growth factor 2 (FGF2), transforming growth factor-β1 (TGF-β1), and collagen type 1 in the rat dental pulp.
Materials And Methods: The first maxillary molars of were perforated and subsequently pulp capped with CaCO extracted from shells.
Glass Ionomer Cement Restoration Technique for Severe Molar Incisor Hypomineralization.
J Dent Child (Chic)
September 2024
Brazilian Dental Association, all in Natal, Rio Grande do Norte, Brazil.
Article Synopsis
- The management of molar-incisor hypomineralization is complex due to varying clinical appearances and treatment needs.
- The report details a treatment case involving a carious permanent molar using glass ionomer cement (GIC) and an occlusal replica technique.
- After the procedure, the patient showed no symptoms, maintained good oral hygiene, and the restorative material remained intact after 12 months.
Effect of cementation technique and cement type on the amount of excess cement in implant-supported cement-retained crown restorations: An in vitro study.
J Prosthet Dent
December 2024
Professor, Department of Prosthodontics, Faculty of Dentistry, Gazi University, Ankara, Turkey.
Statement Of Problem: Excess cement in implant-supported restorations can lead to peri-implant diseases, and its removal remains a clinical challenge. The optimum method of minimizing excess cement is unclear.
Purpose: The purpose of this in vitro study was to compare 3 cementation techniques and 3 cement types and measure excess cement.
Long-Term Dentin Bonding Performance of Universal Adhesives: The Effect of HEMA Content and Bioactive Resin Composite.
J Funct Biomater
December 2024
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo 060-8586, Japan.
This study investigated the effects of resin composites (RCs) containing surface pre-reacted glass ionomer (S-PRG) filler on the dentin microtensile bond strength (μTBS) of HEMA-free and HEMA-containing universal adhesives (UAs). Water sorption (WS) and solubility (SL), degree of conversion (DC), and ion release were measured. The UAs BeautiBond Xtreme (BBX; 0% HEMA), Modified Adhesive-1 (E-BBX1; 5% HEMA), Modified Adhesive-2 (E-BBX2; 10% HEMA), and two 2-step self-etch adhesives (2-SEAs): FL-BOND II (FBII; with S-PRG filler) and silica-containing adhesive (E-FBII) were used.
View Article and Find Full Text PDFEvaluation of the Effects of Thermal Aging on the Surface Roughness of Novel Tooth-Colored Restorative Materials.
Dent J (Basel)
December 2024
Department of Biomedical Sciences, School of Dental Medicine, University of Nevada, Las Vegas, NV 89557, USA.
The development of composite resins has led to novel materials aimed at improving restoration longevity. This study evaluates the surface roughness of four tooth-colored restorative materials after thermal aging. Eighty Class V preparations were restored with Admira Fusion, Beautifil II, Equia Forte HT, and Filtek.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!