Introduction: The purpose of this study was to evaluate the effect of acid etching on the compressive strength of 4 calcium silicate-based cements.
Methods: One gram of each corresponding powder of ProRoot MTA (Dentsply Tulsa Dental, Johnson City, TN), MTA Angelus (Angelus, Londrina, PR, Brazil), and CEM cement (BioniqueDent, Tehran, Iran) and a 0.33-g aliquot of liquid were placed in a plastic mixing capsule that was then mechanically mixed for 30 seconds at 4500 rpm in an amalgamator. For the preparation of Biodentine (Septodont, Saint Maur-des-Fossés, France), the liquid provided was added to the powder within the plastic capsule supplied by the manufacturer and then mechanically mixed for 30 seconds at 4500 rpm using the amalgamator. The resulting slurries were then placed incrementally into 40 cylindrical molds to give a total of 160 specimens that were incubated at 37°C for a week. Twenty specimens of each material were then subjected to the acid etch procedure. The compressive strength of the samples was then calculated in megapascals using a universal testing machine. The results were then subjected to 2-way analysis of variance analysis of variance followed by the Tukey post hoc test.
Results: The application of acid etch significantly reduced (P < .0001) the compressive strength of Angelus MTA and CEM cement; however, it did not reduce the compressive strength of ProRoot MTA or Biodentine. Regardless of the acid etch application, Biodentine showed significantly higher compressive strength values than the other materials (P < .0001), whereas CEM cement had the lowest compressive strength values. There was no significant difference between CEM cement and MTA Angelus. The compressive strength of ProRoot MTA was significantly lower (P < .0001) than Biodentine but significantly higher (P < .0001) than MTA Angelus and CEM cement in both the test and control groups.
Conclusions: When the application of acid etchants is required, Biodentine and ProRoot MTA seem to be better options than MTA Angelus or CEM cement.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.joen.2013.09.008 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Investigations on mineralogical characteristics and feasibility of coal gangue as a concrete aggregate from guizhou province, China.
Sci Rep
December 2024
Mining College, Guizhou University, Guiyang, 550025, China.
Coal gangue (CG) is an industrial solid waste produced by coal mining and separation that is considered to have a significant effect on the soil or water environment when exposed to the air, exacerbating ecological pollution. The comprehensive utilization of CG has always been a difficult problem due to the complex mineralogical characteristics. Producing concrete aggregates with CG is an effective strategy for utilising CG resources synthetically.
View Article and Find Full Text PDFInulin biopolymer as a novel material for sustainable soil stabilization.
Sci Rep
December 2024
Geotechnical Institute, TU Bergakademie Freiberg, Freiberg, Germany.
The development of new urban areas necessitates building on increasingly scarce land, often overlaid on weak soil layers. Furthermore, climate change has exacerbated the extent of global arid lands, making it imperative to find sustainable soil stabilization and erosion mitigation methods. Thus, scientists have strived to find a plant-based biopolymer that favors several agricultural waste sources and provides high strength and durability for sustainable soil stabilization.
View Article and Find Full Text PDFDesign and mechanical properties analysis of drill pipe's joint thread with unequal taper under complex loads.
Sci Rep
December 2024
School of Mechanical Engineering, Yangtze University, Jingzhou, 434023, China.
The design of drill pipe joint thread with unequal taper is proposed to investigate the fracture failure of the API NC38 used in the drill pipe joint of the SU36-8-4H2 well. The effect of changes in thread taper on the stress distribution and mechanical properties of drill pipe joints is analyzed and compared with the API standard thread to determine the optimal thread structure with unequal taper. The results reveal highly concentrated stress at the last engaged thread root of API NC38 single-shoulder thread (SUT) may cause early yield failure of the joint threads.
View Article and Find Full Text PDFStudy on uniaxial compression mechanical properties of 3D printed columnar joint test blocks.
Sci Rep
December 2024
College of Civil Engineering and Transportation, Hohai University, Nanjing, 210098, China.
The columnar joint skeleton of 3D printed Acrylonitrile Butadiene Styrene (ABS) material, the skeleton of cement mortar and ultraviolet aging treatment are combined to pour the columnar joint rock mass (CJRM) test block. The strength, deformation, energy and failure modes of the specimens with different dip angles were analyzed by uniaxial compression test. The influence of joint skeleton on the strength of the test block was analyzed.
View Article and Find Full Text PDFFused deposition modeling process parameter optimization on the development of graphene enhanced polyethylene terephthalate glycol.
Sci Rep
December 2024
Centre for Sustainable Materials and Surface Metamorphosis, Chennai Institute of Technology, Chennai, 600069, Tamilnadu, India.
This study investigates the production of graphene-enhanced polyethylene terephthalate glycol (G-PETG) components using fused deposition modeling (FDM) and evaluates their mechanical properties, contributing to the advancement of additive manufacturing. Trials demonstrated notable improvements in mechanical performance, with optimal printing parameters identified using the Spice Logic Analytical Hierarchy Process (AHP). The effectiveness of this methodology is further compared with the Fuzzy Analytic Hierarchy Process (FAHP) combined with the Technique for Order of Preference by Similarity to Ideal Solution (TOPSIS).
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!