Published: April 2013
Objective: To investigate the durability of self-etch adhesives bonded to dentin in vitro.
Methods: Forty-two extracted human molars were selected and occlusal dentin surfaces were exposed. The teeth were randomly distributed into three groups based on adhesives applied. The one-step self-etch adhesive B(Adper Prompt) and C(G-Bond) and two-step self-etch adhesive A (Clearfil SE bond) were used. After application of the adhesives to the dentin surfaces, composite crowns were built up, after 24 h water storage, the teeth were sectioned longitudinally into sticks (1.0 mm×1.0 mm bonding area) for microtensile testing or slabs (1 mm thick) for scanning electron microscopec (SEM) observation. Bonding strength (mTBS) and nano-leakage were evaluated immediately after cutting or after 6 months in water. The mTBS was analyzed using one-way ANOVA (SPSS 13.0). The nanoleakage was observed by SEM with a backscattered electron detector.
Results: Both adhesives and water storage time affected the mTBS. All adhesives showed decreased bond strength after six-month water aging [A dropped from (40.60 ± 5.76) MPa to (36.04 ± 3.15) MPa; B dropped from (19.06 ± 1.50) MPa to (11.19 ± 1.97) MPa; C dropped from (17.75 ± 1.10) MPa to (9.14 ± 1.15) MPa] (P < 0.05). B and C showed lower mTBS than A after aging (P < 0.05). Compared to A, nanoleakage was more obvious after aging for B and C.
Conclusions: All self-etch adhesives tested were probably influenced by water aging, however, the two-step adhesive showed better durability than the one-step adhesives.
Download full-text PDF |
Source |
---|
Int J Dent
January 2025
Department of Orthodontics, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran.
This research aimed to assess the shear bond strength (SBS) of metal brackets bonded to composite veneers using different surface preparations. One-hundred composite disks were divided into 10 different groups whereby each group combines a surface preparation (roughening or no roughening), etching agent (37% phosphoric or 9.5% hydrofluoric acid), adhesive protocol (self-etch or total-etch), and bonding agent (with or without G-Premio Bond).
View Article and Find Full Text PDFJ Funct Biomater
January 2025
Restorative Dentistry Department, Faculty of Dentistry, Gazi University, 06510 Ankara, Turkey.
The aim of this study is to evaluate the shear bond strength of different universal adhesives applied to intact, demineralized, and remineralized enamel surfaces with total-etch and self-etch modes and to examine the effect of universal adhesives on the Ca/P mineral atomic and mass ratios of these enamel with FE-SEM/EDX (Field Emission Scanning Electron Microscopy with Energy Dispersive X-Ray Spectroscopy) analysis. For this study, 264 bovine incisors were used. Samples in the demineralized and remineralized groups were kept in demineralization solution at 37 °C for 96 h to make an artificial initial carious lesion.
View Article and Find Full Text PDFDent J (Basel)
December 2024
Prosthetic Dentistry Discipline, Department 4-Prosthodontics and Dental Materials, Faculty of Dental Medicine, "Iuliu Hațieganu" University of Medicine and Pharmacy, 400012 Cluj-Napoca, Romania.
Air particle abrasion (APA) is a common surface preparation method in dentistry, particularly for improving bond strength to dentin. This review evaluates the influence of APA on dentin adhesion. : A systematic literature search from 2018 to 2023 was conducted according to PRISMA-ScR guidelines.
View Article and Find Full Text PDFBMC Oral Health
January 2025
Conservative Department, Faculty of Dentistry, Kafr Al Sheikh University, Kafr Al Sheikh, Egypt.
Background: Short dentin etching, a relatively recent technique, aims to improve resin-dentin bonding by preserving hydroxyapatite crystals within the collagen spaces. This study explores short dentin etching's potential in mitigating over-etching issues in deep proximal dentin/cementum margins, an aspect not previously investigated. This study evaluates the microtensile bond strength (μTBS) and marginal adaptation of two universal adhesives using different etch-and-rinse strategies (15-second and 3-second etching) and self-etch strategies, both immediate and post-thermal cycling and mechanical loading.
View Article and Find Full Text PDFBMC Oral Health
January 2025
Faculty of Dentistry, Department of Restorative Dentistry, Gazi University, Bişkek St. 1. St. Number: 8 Emek, Ankara, Turkey.
Background: Repairing composite resins is a less invasive alternative to complete restoration replacement. To achieve a successful bond between the existing and newly applied composite materials, various surface preparation methods, such as sandblasting and acid etching, have been explored. The aim of the study was to evaluate the effect of different surface treatments on the repair bond strength of a universal nanohybrid composite resin restorative material before and after thermal aging, by utilizing a micro-shear bond strength (µSBS) test.