A carbon coated Co-SiC nanocomposite was fabricated via in situ pyrolysis of methane on a hierarchical Co3O4-SiC nanostructure, which was obtained by hydrothermal synthesis. By the reduction of methane, the Co3O4 was in situ converted to cobalt nanoparticles, and coated by carbon or filled in the CNTs. The as-prepared composite exhibits excellent microwave absorption performance in the frequency range of 2-18 GHz. When the match thickness is 1.8 mm, the composite has a reflection loss value below -10 dB in the range 12.2 to 18 GHz, which nearly covers the whole Ku-band (12-18 GHz). When the thickness is 2.6 mm, the reflection loss value below -10 dB distributes at 8.2-11.5 GHz, covering most of the X-band (8-12 GHz). Moreover, by further tuning the match thickness, the composite can selectively absorb some certain frequency bands of microwaves.
The synthesis of polymer/oligomer-stabilized metal nanostructures (MNS) opens up a wide range of possibilities, from fundamental materials science to practical applications in domains such as medicine, catalysis, sensing, and energy. Because of the versatility of this synthetic approach, it is a dynamic and ever-changing field of study. These polymers/oligomers have precise control over the nucleation and growth kinetics, allowing the production of mono-disperse MNS with well-defined properties.
Nickel oxide (NiO) is known for its remarkable theoretical specific capacity, making it a highly appealing option for electrode materials in electrochemical energy storage applications. Nevertheless, its practical use is limited by poor electrochemical performance and complicated electrode fabrication processes. To address these issues, we propose a new anode design comprising an intermediate NiO nanoarray layer and a carbon coating layer grown directly on a three-dimensional (3D) conductive nickel foam substrate, designated as C@NiO@Ni foam.
The commercialisation of PEM water electrolysis is still hindered by the necessity of using noble metals that are rare, expensive and therefore unsustainable. To replace the benchmark HER catalyst Pt with more abundant materials, promising non-noble catalysts need to be identified and optimal electrode preparation and electrolysis conditions need to be transferred between catalyst materials to reveal their full potential under industrially relevant conditions. This study investigates the optimal ink composition for spray-coating the cathode regarding the effects on electrode structure, performance and catalyst layer composition.
South China University of Technology, School of Environment and Energy, Room 316, B5 Building, South China University of Technology, Guangzhou Higher Education Mega Center, 510006, Guangzhou, CHINA.
Na4Fe3(PO4)2P2O7 (NFPP) has been regarded as the promising cathode material for sodium-ion batteries (SIBs). However, the practical applications of NFPP are hindered by its high-volume changes, poor intrinsic electron conductivity and sluggish Na+ ions diffusion kinetics. Herein, a spray-drying and solid-state reaction method have been utilized to fabricate the spherical trace amount Mg/Cu co-doped Na4Fe3(PO4)2P2O7 (NFMCPP).
Magnetic liquid metal droplets, featured by unique fluidity, metallic conductivity, and magnetic reactivity, are of growing significance for next-generation flexible electronics. Conventional fabrication routes, which typically incorporate magnetic nanoparticles into liquid metals, otherwise encounter the pitfall pertaining to surface adhesivity and corrosivity over device modules. Here, an innovative approach of synergizing liquid metals with 2D magnetic materials is presented, accordingly creating chromium(III)-telluride-coated liquid metal (CT-LM) droplets via a simple self-assembly process.