Sealing ability of mineral trioxide aggregate, calcium phosphate and polymethylmethacrylate bone cements on root ends prepared using an Erbium: Yttriumaluminium garnet laser and ultrasonics evaluated by confocal laser scanning microscopy.

Background: Surgical endodontic therapy comprises of exposure of the involved root apex, resection of the apical end of the root, preparation of a class I cavity, and insertion of a root end filling material. Mineral trioxide aggregate (MTA) is now the gold standard among all root end filling materials. MTA is however difficult to handle, expensive and has a very slow setting reaction.

Aim: (1) To compare the sealing ability of MTA, polymethylmethacrylate (PMMA) bone cement and CHITRA Calcium phosphate cement (CPC) when used as root end filling material using Rhodamine B dye evaluated under a confocal laser scanning microscope. (2) To compare the seal of root ends prepared using an ultrasonic retroprep tip and an Er: YAG laser using three different root end filling materials.

Statistical Analysis: Statistical analysis was performed using a one-way ANOVA and a two-way ANOVA, independent samples t-test and Scheffe's post hoc test using SPSS Version 16 for Windows.

Results: All the three materials, namely MTA, PMMA BONE CEMENT and CHITRA CPC, showed microleakage. Comparison of microleakage showed maximum peak value of 0.86 mm for MTA, 0.24 mm for PMMA bone cement and 1.37 mm for CHITRA CPC. The amount of dye penetration was found to be lesser in root ends prepared using Er: YAG laser when compared with ultrasonics, but the difference was found to be not statistically significant.

Conclusion: PMMA bone cement is a better material as root end filling material to prevent apical microleakage. MTA still continues to be a gold standard root end filling material showing minimum microleakage. Er: YAG laser is a better alternative to ultrasonics for root end preparations.