Sea urchin like shaped cdse nanoparticles grown in aqueous solutions via electron beam irradiation.

Cadmium selenide (CdSe) nanoparticles have been grown from an aqueous solutions containing equimolar ammoniated cadmium sulphate and sodium selenosulphate as precursors in presence of citric acid as a capping agent, via electron beam irradiation. The radiolytic processes occurring in the medium result in the formation of CdSe nanoparticles through the reactions mediated by hydrated electrons (e(aq)-). The dynamics of the formation of these nanoparticles was investigated by pulse radiolysis studies. The size of the primary nanoparticles as estimated from the absorption spectra recorded immediately was less than 3 nm. These nanoparticles exhibited strong excitonic absorption pattern and broad photoluminescence at room temperature, which has been attributed to the presence of surface states/defects. This has been confirmed by Raman spectral studies, where CdSe nanoparticles exhibited characteristic surface phonon modes at around 250 cm(-1). The photoluminescence lifetime decay measurements further supported the existence of surface defects on the as-grown CdSe nanoparticles. These nanoparticles were found to exist in the agglomerated form of sea urchin like shapes of uniform size of about 500 nm as revealed from TEM and SEM images. These sea urchin like shaped CdSe nanoparticles grown in this route were found to be very stable under the ambient conditions. We infer that citric acid influences the growth as well as stability of these nanoparticles. It is expected that these nanomaterials could find potential applications in the field of sensors, catalysis and photovoltaics.