Broadband infrared light-emitting patterns in optical glass by laser-induced nanostructuring of NiO-doped alkali-gallium germanosilicates.

In this Letter, we show functionalization of NiO-doped 7.5Li(2)O·2.5Na(2)O·20Ga(2)O(3)·35SiO(2)·35GeO(2) glass by space-selective nanocrystallization via exposure to the focused beam of a pulsed copper vapor laser (510.6 and 578.2 nm) at temperature close to the glass transition point (570°C). Irradiated areas drastically change their color, caused by electronic transitions of Ni(2+) dopant ions, without any alteration of the optical quality. Importantly, irradiated regions acquire broadband infrared luminescence (centered at about 1400 nm and possessing 400 nm effective bandwidth) typical of Ni(2+) ions in crystalline environment, and by positive change of refractive index (more than 10(-3)). Spectroscopic and diffractometric data of the irradiated regions indeed resemble those previously observed in thermally nanocrystallized glass, with Ni(2+) ions embedded in γ-Ga(2)O(3) nanocrystals. The results demonstrate the possibility of laser writing nanocrystallized multifunction patterns in germanosilicate glasses for the fabrication of active integrated devices.