Diffusion mechanism of exchange bias formation in permalloy-manganese nanostructures at thermo-magnetic treatment.

A mechanism of unidirectional exchange anisotropy formation at thermo-magnetic treatment of permalloy-manganese bilayers has been studied. A shift of hysteresis loops appears at annealing beginning from 230 degrees C. The maximal exchange field of 155 Oe is reached after the 250 degrees C annealing for 2 h. As demonstrated by transmission electron microscopy, the exchange bias and the coercivity growth result from an ordered anti-ferromagnetic NiFeMn phase formation due to the diffusion interaction of permalloy and manganese at annealing.