Enhancement of hydrogen gas sensing of nanocrystalline nickel oxide by pulsed-laser irradiation.

ACS Appl Mater Interfaces

Nanotechnology and MEMS Laboratory, Department of Mechanical, Industrial and Manufacturing Engineering, The University of Toledo, MS 312, Toledo, Ohio 43606-3390, USA.

Published: September 2012

This paper reports the effect of post-laser irradiation on the gas-sensing behavior of nickel oxide (NiO) thin films. Nanocrystalline NiO semiconductor thin films were fabricated by a sol-gel method on a nonalkaline glass substrate. The NiO samples were irradiated with a pulsed 532-nm wavelength, using a Nd:YVO(4) laser beam. The effect of laser irradiation on the microstructure, electrical conductivity, and gas-sensing properties was investigated as a function of laser power levels. It was found that the crystallinity and surface morphology were modified by the pulsed-laser irradiation. Hydrogen gas sensors were fabricated using both as-deposited and laser-irradiated NiO films. It was observed that the performance of gas-sensing characteristics could be changed by the change of laser power levels. By optimizing the magnitude of the laser power, the gas-sensing property of NiO thin film was improved, compared to that of as-deposited NiO films. At the optimal laser irradiation conditions, a high response of NiO sensors to hydrogen molecule exposure of as little as 2.5% of the lower explosion threshold of hydrogen gas (40,000 ppm) was observed at 175 °C.

Download full-text PDF

Source
http://dx.doi.org/10.1021/am301024aDOI Listing

Publication Analysis

Top Keywords

hydrogen gas
12
laser power
12
nickel oxide
8
pulsed-laser irradiation
8
nio thin
8
thin films
8
laser irradiation
8
power levels
8
nio films
8
nio
7

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!