Tissue-engineered calcium phosphate cement in rabbit femoral condylar bone defects.

Background: Calcium phosphate cement (CPC) is a favorable bone-graft substitute, with excellent biocompatibility and osteoconductivity. However, its reduced osteoinductive ability may limit the utility of CPC. To increase its osteoinductive potential, this study aimed to prepare tissue-engineered CPC and evaluate its use in the repair of bone defects. The fate of transplanted seed cells in vivo was observed at the same time.

Methods: Tissue-engineered CPC was prepared by seeding CPC with encapsulated bone mesenchymal stem cells (BMSCs) expressing recombinant human bone morphogenetic protein-2 (rhBMP-2) and green fluorescent protein (GFP). Tissue-engineered CPC and pure CPC were implanted into rabbit femoral condyle bone defects respectively. Twelve weeks later, radiographs, morphological observations, histomorphometrical evaluations, and in vivo tracing were performed.

Results: The radiographs revealed better absorption and faster new bone formation for tissue-engineered CPC than pure CPC. Morphological and histomorphometrical evaluations indicated that tissue-engineered CPC separated into numerous small blocks, with active absorption and reconstruction noted, whereas the residual CPC area was larger in the group treated with pure CPC. In the tissue-engineered CPC group, in vivo tracing revealed numerous cells expressing both GFP and rhBMP-2 that were distributed in the medullar cavity and on the surface of bony trabeculae.

Conclusion: Tissue-engineered CPC can effectively repair bone defects, with allogenic seeded cells able to grow and differentiate in vivo after transplantation.