Purpose: Candida-associated denture stomatitis is the most prevalent form of oral candidosis affecting 65% of denture wearers. Failure of therapy and recurrence of infection are not uncommon and the continuous use of antifungal agents may affect the surface properties of the denture material and may contribute to Candida adhesion. This study aimed to investigate surface properties of poly(methyl methacrylate) PMMA denture material before and after exposure to antifungal agents and its relation to in vitro adhesion of Candida albicans.
Methods: Four groups of acrylic specimens (20 mm × 20 mm × 2.5mm) were prepared (25 specimens in each group). Specimens were immersed in nystatin (group 1), fluconazole (group 2), distilled water (group 3) and group 4 was not exposed. Specimens were tested for surface roughness, contact angle, surface hardness and in vitro Candida adherence to PMMA.
Results: The results showed that nystatin had no statistically significant effect on surface hardness (P>0.05), but had a statistically significant effect on surface roughness, contact angle, and Candida adhesion to PMMA (P<0.05). On the other hand, fluconazole had no statistically significant effect on surface hardness or roughness (P>0.05), but had a statistically significant effect on contact angle, and Candida adhesion to PMMA (P<0.05). Distilled water had no statistically significant effect on surface hardness, roughness, contact angle, or Candida adhesion to PMMA (P>0.05).
Conclusions: Exposure of PMMA to nystatin may induce changes in roughness, wettability while exposure to fluconazole may affect surface free energy and therefore may increase Candida adhesion to it.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.jpor.2012.02.006 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effects of the Tobacco Defensin NaD1 Against Susceptible and Resistant Strains of .
Pathogens
December 2024
M.M. Shemyakin and Yu.A. Ovchinnikov Institute of Bioorganic Chemistry, Russian Academy of Sciences, 117997 Moscow, Russia.
Today, is still the most common cause of both local and life-threatening systemic candidiasis. The spread of resistant fungal strains has resulted in an urgent need to search for new promising antimycotics. Here, we investigated the antifungal action of the tobacco defensin NaD1 against susceptible and resistant to azoles and echinocandins strains of .
View Article and Find Full Text PDFThe Effect of Medium-Chain Triglycerides Oil on and in Planktonic and Mucosal Models.
Antibiotics (Basel)
December 2024
Eastman Institute for Oral Health, University of Rochester Medical Center, Rochester, NY 14642, USA.
Despite MCT oil's potential antimicrobial benefits for gastrointestinal health, its effects on disrupting cariogenic pathogens on oral mucosal surfaces remain underexplored. This study evaluated the impact of MCT oil on the adhesion and invasion of and using planktonic and mucosal models. First, a planktonic model was used to assess the impact of various concentrations of MCT on the growth of and .
View Article and Find Full Text PDFPrinted versus heat-polymerized resin for occlusal devices: Evaluation of physical and mechanical properties after brushing and microbial adhesion.
J Prosthodont
January 2025
Department of Dental Materials and Prosthesis, Ribeirão Preto Dental School, University of São Paulo (USP), Ribeirão Preto, Brazil.
Purpose: To evaluate the physical and mechanical properties after brushing and microbial adhesion of printed resins (PRs) and heat-polymerized resins (HRs) for occlusal devices (ODs).
Materials And Methods: Knoop microhardness and roughness were evaluated in three measurements before and after brushing with detergent or dentifrice. Flexural strength and modulus of elasticity were assessed by 3-point bending, and the adhesion of Candida albicans and Streptococcus mutans was evaluated by colony-forming units per milliliter (CFU/mL) and metabolic activity using the XTT assay only without brushing.
Polydimethylsiloxane loaded capsaicin afflicts membrane integrity, metabolic activity and biofilm formation of nosocomial pathogens.
Microb Pathog
January 2025
Biofouling and Biofilm Processes Section, Water and Steam Chemistry Division, Bhabha Atomic Research Centre Facilities, Kalpakkam, 603 102, India; Homi Bhabha National Institute, Anushaktinagar, Mumbai, 400 094, India. Electronic address:
Biofilms constitute 80 % of all nosocomial infections associated with invasive medical devices. Polydimethylsiloxane, a highly elastic, inert, non-reactive, biocompatible silicone polymer is widely used as implant biomaterial due to its non-toxic and low-immunogenic nature. Owing to its hydrophobicity, PDMS suffers from microbial adhesion.
View Article and Find Full Text PDFEffect of nanogold incorporation into polymethyl methacrylate denture bases on microbial activity in implant-retained mandibular overdentures.
Int J Implant Dent
January 2025
Lecturer at removable prosthodontic department, Faculty of dental medicine for Girls, Al-Azhar University, Cairo, Egypt.
Article Synopsis
- A clinical trial tested the effectiveness of adding nanogold particles to denture bases made of polymethyl methacrylate (PMMA) against standard acrylic bases, focusing on their impact on bacterial growth.
- Twenty-two male patients with no teeth received either traditional acrylic dentures or those enhanced with nanogold, and microbial growth was measured over time around the implants.
- Results showed that dentures with nanogold significantly reduced bacteria counts (Candida albicans, Escherichia coli, and Streptococcus mutans) at 2, 4, and 6 months compared to traditional dentures, suggesting a promising improvement in oral hygiene.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!