Shear bond strength of different repair systems to titanium after water aging.

This study evaluated the shear bond strength (SBS) and stability of commercially pure titanium (CP Ti)/repair material interfaces promoted by different repair systems. One hundred CP Ti cast discs were divided into five repair system groups: 1) Epricord (EP); 2) Bistite II DC (BT); 3) Cojet (CJ); 4) Scotchbond Multi-Purpose Plus (SB) (control group); and 5) Cojet Sand plus Scotchbond Multi-Purpose Plus (CJSB). The specimens were stored in distilled water for 24 hours at 37°C, thermal cycled (5000 cycles, 5°-55°C) and stored under the same conditions for either 24 hours or six months (n=10). SBS was tested and the data were analyzed by two-way analysis of variance (ANOVA) and Tukey test (α=.05). Failure mode was determined with a stereomicroscope (20×). The repair system, storage time, and their interaction significantly affected the SBS (p<0.001). At 24 hours, CJSB exhibited the highest SBS value, followed by CJ. At six months, these two groups had similar mean SBS (p>0.05) and higher means in comparison to the other groups. For both storage times, BT presented the lowest SBS, while the EP and SB groups did not differ significantly from one another (p>0.05). There were no significant differences in SBS between the storage times for the groups EP and CJ (p>0.05). The groups BT, SB, and CJSB showed 100% adhesive failure, irrespective of storage time. The CJSB group showed the highest SBS at both storage times. At six months, the CJ group exhibited a similar SBS mean value when compared to the CJSB group. Water storage adversely affected the groups BT, SB (control group), and CJSB. Considering SBS values, stability, and the failure mode simultaneously, the CJ group showed the best CP Ti repair performance.