Increases in solar conversion efficiencies of the ZrO2 nanofiber-doped TiO2 photoelectrode for dye-sensitized solar cells.

In this paper, in order to improve the efficiency of dye-sensitized solar cells, we introduced zirconia [ZrO2] nanofibers into a mesoporous titania [TiO2] photoelectrode. The photoelectrode consists of a few weight percent of ZrO2 nanofibers and a mesoporous TiO2 powder. The mixed ZrO2 nanofibers and the mesoporous TiO2 powder possessed a larger surface area than the corresponding mesoporous TiO2 powder. The optimum ratio of the ZrO2 nanofiber was 5 wt.%. The 5 wt.% ZrO2-mixed device could get a short-circuit photocurrent density of 15.9 mA/cm2, an open-circuit photovoltage of 0.69 V, a fill factor of 0.60, and a light-to-electricity conversion efficiency of 6.5% under irradiation of AM 1.5 (100 mW/cm2).