Alkylated graphene nanosheet composites with polyaniline nanofibers.

We demonstrate a simple method to prepare alkylated graphene/polyaniline composites (a-GR/PANI) using solution mixing of exfoliated alkyl Iodododecane treated graphene oxide sheets with polyaniline nanofiber; polyaniline nanofibers (PANI) prepared by using rapid mixing polymerization significantly improve the processibility of polyaniline and its performance in many conventional applications. Also, polyaniline nanofibers exhibit excellent water dispersibility due to their uniform nanofiber morphology. Morphological study using SEM and TEM analysis showed that the fibrous PANI in the composites a-GR/PANI mainly adsorbed onto the surface or intercalated between the graphene sheets, due especially to the good interfacial interaction between the alkylated gaphene and the polyaniline nanofibers. The existence of polyaniline nanofibers on the surface of the garphene and the alkylated graphene sheets was confirmed by using FT-IR, FT-Raman and X-ray diffraction analysis. Due to the good interfacial interaction between the alkylated graphene and the polyanilines nanofibers, the composite (a-GR/PANI) exhibited excellent dispersion stability in DMF compared to the same composite (GR/PANI) without alkylation. The electrical conductivity of the (GR/PANI) composite was 9% higher than that of pure PANI and the same weight percent for the composite after alkylation was 13% higher than that of pure PANI nanofibers.