Objectives: This study assessed the fatigue resistance and failure mode of type III porcelain and composite resin veneers bonded to custom composite resin implant abutments.
Material And Methods: Using the CEREC 3 machine, 28 composite resin implant abutments (Paradigm MZ100) were fabricated along with non-retentive type III veneers, milled either in ceramic Paradigm C (n=14) or in composite resin Paradigm MZ100 (n=14). The intaglio surfaces of the veneers were hydrofluoric acid etched and silanated (Paradigm C) or airborne-particle abraded and silanated (MZ100). The fitting surface of the abutments was airborne-particle abraded, cleaned, silanated and inserted into a bone level implant (10 mm, BLI RC). All veneers were luted with adhesive resin (Optibond FL) and a preheated light curing composite resin (Filtek Z100). Cyclic isometric chewing (5 Hz, 30° angle) was simulated, starting with a load of 40 N, followed by stages of 80, 120, 160, 200, 240 and 280 N (20,000 cycles each). Samples were loaded until fracture or to a maximum of 140,000 cycles. Groups were compared using the life table survival analysis (Log rank test at P=0.05). Previously published data using same-design zirconia abutments were included for comparison.
Results: Paradigm C and MZ100 specimens fractured at an average load of 243 and 206 N (survival rate of 21% and 0%), respectively, with a significant difference in survival probability (P=0.02). Fractured specimens presented mixed failure modes and solely adhesive failures were not observed. The survival of composite resin abutments was similar to that of identical zirconia abutments from a previous study (P=0.76).
Conclusions: Non-retentive porcelain veneers bonded to custom composite resin implant abutments presented a higher survival rate when compared with composite resin veneers. Survival of composite resin abutment did not differ from zirconia ones.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1111/j.1600-0501.2010.02103.x | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
[How I treat… An open bite secondary to ankylosis of a primary molar tooth].
Rev Med Liege
January 2025
Service de Dentisterie conservatrice, endodontie et pédodontie, CHU Liège, Belgique.
Infraclusion is a consequence of dentoalveolar ankylosis. Associated complications include extrusion of the opposing tooth, open bites, and tilts. Early detection and management are crucial to limit and/or correct these complications.
View Article and Find Full Text PDFEvaluation of the effect of different irrigation solutions used in regenerative endodontic treatment of necrotic molar teeth with open apex on postoperative pain- randomized clinical trial.
Clin Oral Investig
January 2025
Department of Pedodontics, Faculty of Dentistry, Erciyes University, 38039, Kayseri, Türkiye.
Objectives: This study evaluates the effect of different irrigation solutions for postoperative pain in the regenerative endodontic treatments (RET) of necrotic teeth with open apex.
Materials And Methods: This study included necrotic, deeply carious lower molars of 42 patients. Access cavities of the teeth were opened and working lengths were measured at the first visit.
Bond strength to eroded dentin as per chlorhexidine use for controlling erosive wear or interface aging: an 18-month assay.
Braz Oral Res
January 2025
Universidade de São Paulo - USP, School of Dentistry, Department of Operative Dentistry, São Paulo, SP, Brazil.
The aim of this study was to assess the effect of a chlorhexidine digluconate solution (CHX) applied as an antiproteolytic agent for controlling erosive tooth wear or as part of the adhesive treatment on long-term bond strength to eroded dentin. Dentin specimens were abraded with a 600-grit silicon carbide (SiC) paper for 1 min (sound dentin - S), subsequently treated with 2% CHX for 1 min (with excess removed, followed by a 6-hour rest), and eroded by exposure to Coca-Cola for 5 min, three times a day, for 5 days (CHX-treated and eroded dentin - CHXE), or only eroded (eroded dentin - E). The specimens were acid-etched (15 s), rinsed (30 s), dried (15 s), and rehydrated with 1.
View Article and Find Full Text PDFDouble-vestibular incision subperiosteal tunnel access (double-VISTA) with connective tissue graft for treating multiple gingival recessions: 2-year follow-up.
Clin Adv Periodontics
January 2025
Department of Orofacial Sciences, School of Dentistry, University of California San Francisco, San Francisco, California, USA.
Background: Gingival recession has a multifactorial etiology, involving various predisposing and precipitating factors. Non-carious cervical lesions (NCCLs) are often associated with gingival recession and pose challenges due to their complex pathodynamics. There is limited evidence regarding tunnel-based procedures combined with connective tissue grafts (CTGs) for treating recession-associated NCCLs.
View Article and Find Full Text PDFOutcome of Er, Cr:YSGG laser and antioxidant pretreatments on bonding quality to caries-induced dentin.
BMC Oral Health
January 2025
Conservative Dentistry Department, Faculty of Oral and Dental Medicine, Future University, Cairo, Egypt.
Background: This study aimed to assess the influence of different pretreatment protocols and antioxidants application on the shear bond strength (SBS) of universal adhesive to sound (SoD) and caries-induced dentin (CID).
Methods: One hundred and twenty posterior teeth had their occlusal enamel removed, then the specimens were divided into two main groups according to dentin substrates; SoD and CID, three subgroups according to pretreatments protocols control (no pretreatment), NaOCl-treated, and Er, Cr:YSGG-treated and two divisions according to antioxidant application (with and without sodium ascorbate (SA) application). All-Bond Universal (ABU) universal adhesives was applied in self-etch (SE) mode then resin composite discs were built.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!