Objectives: To determine the biomechanical characteristics of septal cartilage (SC) and costal cartilage (CC) taken from fresh cadavers using tensile testing and to establish CC graft material of a suitable thickness (ie, with tensile characteristics closest to those of SC).
Methods: Grafts of varying thickness were harvested from the central part of the seventh-rib CC and SC of 18 fresh cadavers. Tensile testing was performed with a 0.5-kilonewton load calibrated at 7 mm/min. The results were shown as a force-elongation curve.
Results: No significant difference according to tensile force was observed between the SC group and the 1.0-mm and 1.5-mm CC groups (P = .09 and P = .32, respectively). However, a significant difference was observed between the SC group and the 2.0-mm CC group (P = .04). Although the strength value of the CC group was 5.03 MPa, the modulus of elasticity was 1.33 MPa. In the SC group, the strength value was 12.42, but the modulus of elasticity was 1.39 MPa. The strength value of the SC group was higher than that of the CC group (P = .001), but the modulus of elasticity value of the CC group was higher than that of the SC group (P = .001).
Conclusions: From the standpoint of tensile testing for preparing columellar struts, 1.0-mm and 1.5-mm CC have similar characteristics to SC and thus can be used instead of it. However, it is important to determine the thickness of CC by considering the expected characteristics of the established material and the forces that affect the area in the nose where the graft will be placed.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1001/archfacial.2011.54 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Research on correlation analysis and multivariate nonlinear regression modeling method for the tensile properties of mugwort petiole.
Sci Rep
December 2024
College of Mechanical Engineering, Hubei University of Technology, Wuhan, Hubei, 430068, China.
The defoliation quality of mugwort defoliation equipment is an important factor to measure the defoliation efficiency, and the tensile properties of mugwort petiole will have an impact on the defoliation quality, such as the crushing rate and the abscission rate. In order to reduce the crushing rate and improve the abscission rate during mechanical harvesting of mugwort leaves, the tensile properties of mugwort petiole need to be studied. The tensile properties of mugwort petiole are closely related to its macroscopic and microscopic physicochemical parameters.
View Article and Find Full Text PDFStrength, durability, and economic analysis of GGBS-based geopolymer concrete with silica fume under harsh conditions.
Sci Rep
December 2024
Civil Engineering Department, Shoolini University, Solan, Himachal Pradesh, 173229, India.
Geopolymer concrete (GPC) offers a sustainable alternative by eliminating the need for cement, thereby reducing carbon dioxide emissions. Using durable concrete helps prevent the corrosion of reinforcing bars and reduces spalling caused by chemical attacks. This study investigates the impact of adding 5, 10, and 15% silica fumes (SF) on the mechanical and durability properties of GPC cured at 60 °C for 24 h.
View Article and Find Full Text PDFPreliminary study on the preparation of lyophilized acellular nerve scaffold complexes from rabbit sciatic nerves with human umbilical cord mesenchymal stem cells.
World J Stem Cells
December 2024
Department of Orthopedics, Children's Hospital of Fudan University & National Children's Medical Center, Shanghai 201102, China.
Background: The gold standard of care for patients with severe peripheral nerve injury is autologous nerve grafting; however, autologous nerve grafts are usually limited for patients because of the limited number of autologous nerve sources and the loss of neurosensory sensation in the donor area, whereas allogeneic or xenografts are even more limited by immune rejection. Tissue-engineered peripheral nerve scaffolds, with the morphology and structure of natural nerves and complex biological signals, hold the most promise as ideal peripheral nerve "replacements".
Aim: To prepare allogenic peripheral nerve scaffolds using a low-toxicity decellularization method, and use human umbilical cord mesenchymal stem cells (hUC-MSCs) as seed cells to cultivate scaffold-cell complexes for the repair of injured peripheral nerves.
Study on interfacial mechanical properties and structural detail damage of CRTS II slab ballastless track.
Sci Rep
December 2024
School of Civil and Hydraulic Engineering, Chongqing University of Science & Technology, Chongqing, 400074, China.
The CRTS (China Railway Track System) II slab ballastless track is widely utilized in high-speed railway construction owing to its excellent structural integrity. However, its interfacial performance deteriorates under high-temperature conditions, leading to significant damage in structural details. Furthermore, the evolution of its performance under these conditions has not been comprehensively studied.
View Article and Find Full Text PDFEnhanced flame retardancy and accelerated degradation of polylactic acid using a chitosan-based additive with phosphorus and zinc.
Int J Biol Macromol
December 2024
State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China. Electronic address:
Polylactic acid (PLA) is a bio-recyclable plastic, but its high flammability limits broader applications. Here, a novel flame retardant (Zn-CHP) is synthesized from chitosan (CH), diethylenetriaminepenta (methylenephosphonic) acid (DTPMP), and ZnCl₂ using a simple, solvent-free process. The Zn-CHP additive is melt-blended with PLA, achieving excellent flame retardancy at just 2 wt% loading.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!