Objective: To compare push-out bond strength of fiber-posts luted with different adhesive approaches to root canal dentin.
Materials And Methods: Forty maxillary first incisors were decoronated and endodontically treated. Specimens were randomly distributed into five groups (n = 8) and fiber-posts (DentinPost coated, Komet) were inserted using five different luting materials: etch-and-rinse adhesive systems and corresponding core-and-post material in groups 1 (DentinBond/DentinBuild, Komet) and 2 (XP Bond + SCA/Core-X flow, Densply), self-adhesive resin cements in groups 3 (RelyX Unicem, 3M Espe) and 4 (SmartCem 2, Dentsply) and a self-etch adhesive/resin cement in group 5 (ED-Primer II/Panavia F 2.0, Kuraray). The roots were sectioned into eight 1 mm thick serial slices and within 48 h push-out bond strength was investigated. Statistical analyses were performed using non-parametrical Kruskal-Wallis H-test and Mann-Whitney U-test for differences between experimental groups at p < 0.05. The failure modes were analyzed using Chi square test.
Results: The bond strength [MPa] (mean/min-max) for groups 3 (12.35/3.60-32.44), 4 (13.52/4.48-30.69) and 2 (11.15/5.23-35.58) were significantly higher (p < 0.001) compared to groups 1 (6.66/2.34-24.89) and 5 (7.41/0.28-34.18). Adhesive failure between dentin and luting agent was the most frequent failure mode.
Conclusions: Bond strength of fiber-posts adhesively luted to root canal dentin was significantly higher when self-adhesive resin cements were used. One (group 2) of the tested core-and-post materials/etch-and-rinse adhesive achieved comparable bond strength values.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3109/00016357.2011.603702 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
In Situ Anchoring Functional Molecules to Polymer Chains Through Supramolecular Interactions for a Robust and Self-Healing Multifunctional Waterborne Polyurethane.
Small
January 2025
Department of Polymer Materials and Engineering, School of Chemical Engineering and Technology, Hebei University of Technology, Tianjin, 300401, P. R. China.
Nowadays, much attention is paid to the development of high-performance and multifunctional materials, but it is still a great challenge to obtain polymer materials with high mechanical properties, high self-healing properties, and multifunctionality in one. Herein, an innovative strategy is proposed to obtain a satisfactory waterborne polyurethane (PMWPU-Bx) by in situ anchoring 3-aminophenylboronic acid (3-APBA) in a pyrene-capped waterborne polyurethane (PMWPU) via supramolecular interactions. The multiple functional sites inherent in 3-APBA can produce supramolecular interactions with groups on PMWPU, promoting the aggregation of hard domains in the polymer network, which confers the PMWPU-Bx strength (7.
View Article and Find Full Text PDFDouble-Dynamic-Bond Cross-Linked Hydrogel Adhesive with Cohesion-Adhesion Enhancement for Emergency Tissue Closure and Infected Wound Healing.
Adv Healthc Mater
January 2025
College of Polymer Science and Engineering, State Key Laboratory of Polymer Materials Engineering, Sichuan University, Chengdu, 610065, China.
The hydrogel adhesives with strong tissue adhesion and biological characteristics adhm202404447are urgently needed for injury sealing and tissue repair. However, the negative correlation between tissue adhesion and the mechanical strength poses a challenge for their practical application. Herein, a bio-inspired cohesive enhancement strategy is developed to prepare the hydrogel adhesive with simultaneously enhanced mechanical strength and tissue adhesion.
View Article and Find Full Text PDFThis study examines the intricate area of refractory-based high entropy alloys (RHEAs), focusing on a series of complex compositions involving nine diverse refractory elements: Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, and W. We investigate the phase stability, bonding interactions, electronic structures, lattice distortions, mechanical, and thermal properties of six RHEAs with varying elemental ratios using VASP and OLCAO DFT calculations. Through comprehensive analysis, we investigate the impact of elemental variations on the electronic structure, interacting bond dynamics, lattice distortion, thermodynamic, mechanical, and thermal properties within these RHEAs, providing an insight into how these specific elemental variations in composition give rise to changes in the calculated properties in ways that would guide future experimental and computational efforts.
View Article and Find Full Text PDFA Microwave-Strengthened Supramolecular Adhesive: from Flexible Pressure Sensitive Bonding to Strong and Muti-Reusable Hot Melt Bonding.
Small
January 2025
Key Laboratory of Organic Optoelectronics & Molecular Engineering, Department of Chemistry, Tsinghua University, Beijing, 100084, P. R. China.
A microwave-strengthened supramolecular adhesive by introducing maleic acid amide bonds into the cross-linked networks of catechol-based monomers and iron oxide nanoparticles is reported. Under microwave irradiation, the supramolecular adhesive can be rapidly heated up, causing the transformation from maleic acid amide bonds to maleimide bonds and thus the increase of its cohesive strength. The supramolecular adhesive can flexibly bond substrates like pressure sensitive adhesives during the bonding procedure and shows an adhesion strength of 0.
View Article and Find Full Text PDFCompletely Multipolar Model for Many-Body Water-Ion and Ion-Ion Interactions.
J Phys Chem Lett
January 2025
Kenneth S. Pitzer Theory Center and Department of Chemistry, University of California, Berkeley, California 94720, United States.
This work constructs an advanced force field, the Completely Multipolar Model (CMM), to quantitatively reproduce each term of an energy decomposition analysis (EDA) for aqueous solvated alkali metal cations and halide anions and their ion pairings. We find that all individual EDA terms remain well-approximated in the CMM for ion-water and ion-ion interactions, except for polarization, which shows errors due to the partial covalency of ion interactions near their equilibrium. We quantify the onset of the dative bonding regime by examining the change in molecular polarizability and Mayer bond indices as a function of distance, showing that partial covalency manifests by breaking the symmetry of atomic polarizabilities while strongly damping them at short-range.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!