Objectives: The aim of this study was to assess the influence of various ceramic thicknesses and luting agents on color variation in five ceramic systems.
Methods: Fifteen disc-shaped ceramic specimens (11 mm diameter; shade A3) were fabricated with each of the six veneering ceramics tested, with 1, 1.5, or 2 mm thickness (n=5). Resin composite discs (Z-250, shade C4) were used as bases to simulate a chromatic background. The cementation of the veneers was carried out with an opaque resin-based cement (Enforce, shade C4), a resin-based cement (Enforce, shade A3), or without cement (C4, control group). Color differences (ΔE*) were determined using a colorimeter. Three-way ANOVA was used to analyze the data, followed by a Tukey post-hoc test (α=.05).
Results: The L*a*b* values of the ceramic systems were affected by both the luting agent and the ceramic thickness (P<.05). In general, there was no difference between the control group and the group using the resin-based cement. The use of an opaque luting agent resulted in an increase of the color coordinates a*, b*, L*, producing differences in ΔE* values for all ceramics tested, regardless of the thickness (P<.05). For the 2-mm thick veneers, higher values in the color parameters were obtained for all ceramics and were independent of the luting agent used.
Conclusions: The association of 2-mm thickness with opaque cement presented the strongest masking ability of a dark colored background when compared to a non- opaque luting agent and the other thicknesses tested.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC3137436 | PMC |
Publication Analysis
Top Keywords
Similar Publications
Novel Foamed Magnesium Phosphate Antimicrobial Bone Cement for Bone Augmentation.
J Biomed Mater Res B Appl Biomater
January 2025
Chongqing Key Laboratory of Oral Diseases and Biomedical Sciences, Chongqing, People's Republic of China.
In dental implant surgery, infection is identified as the primary factor contributing to the failure of bone grafts. There is an urgent need to develop bone graft materials possessing antibacterial characteristics to facilitate bone regeneration. Magnesium phosphate bone cement (MPC) is highly desirable for bone regeneration due to its favorable biocompatibility, plasticity, and osteogenic capabilities.
View Article and Find Full Text PDFEfficacy of different endodontic irrigants in the lesion sterilization and tissue repair technique in primary molars: A randomized controlled clinical trial.
J Indian Soc Pedod Prev Dent
October 2024
Department of Pediatric and Preventive Dentistry, Subharti Dental College and Hospital, Swami Vivekanand Subharti University, Meerut, Uttar Pradesh, India.
Background And Aim: This study aims to evaluate the efficacy of different endodontic irrigants employed in the lesion sterilization and tissue repair (LSTR) technique.
Methods: Forty children aged 4-8 years having at least one primary molar with irreversible pulpitis/pulpal necrosis indicated for pulpectomy were included. Participants were randomly divided into three test groups (Group A, B, and C) and one control group (Group D).
Comparative evaluation of silver diamine fluoride, glass ionomer cement, and calcium hydroxide for indirect pulp therapy in young permanent molars: A randomized controlled trial.
J Indian Soc Pedod Prev Dent
October 2024
Department of Paediatric and Preventive Dentistry, T.P.C.T's Terna Dental College, Navi Mumbai, Maharashtra, India.
Objectives: Comparative evaluation of indirect pulp therapy (IPT) with silver diamine fluoride (SDF), Type VII glass ionomer cement (GIC), and calcium hydroxide (Ca(OH)2) in young permanent molars.
Materials And Methods: This was randomized controlled trial, in which 45 children with 60 young permanent first molars were allocated as; Group A: IPT with SDF, Group B: Type VII GIC, and Group C: Ca(OH)2. Clinical and radiographic evaluation and comparison was done at baseline, 3, 6, 12 months.
Effects of nanosecond‑ and microsecond‑pulse Er, Cr: YSGG laser on the morphology and pulp temperature of dentin in dental restoration debonding.
Lasers Med Sci
January 2025
Department of Stomatology, the First Medical Centre, Chinese PLA General Hospital, Beijing, 100853, China.
Objective: This study evaluated dentin morphology and pulp cavity temperature changes during nanosecond‑ and microsecond‑pulse Er, Cr: YSGG laser debonding restoration and residual adhesive.
Materials And Methods: Ten caries-free teeth had their enamel removed perpendicular to the long axis, followed by bonding of glass ceramic restorations. The samples were randomly divided into two groups and subjected to Er, Cr: YSGG laser (3 mJ, 100 Hz, 100 ns), (3 mJ, 100 Hz, 150 µs) for debonding of restoration and residual adhesive on dentin surfaces.
Shear Strength of Adhesives Based on Solvent Type, Aged, and LED-cured with Different Wavelengths: An Study.
J Contemp Dent Pract
September 2024
Department of Academic, Faculty of Dentistry, Universidad Nacional Federico Villarreal, Lima, Peru, ORCID: https://orcid.org/0000-0002-0594-5834.
Objective: To evaluate the shear strength of adhesives based on the type of solvent (ethanol and acetone), aged and light-cured using light-emitting diode (LED) units with different wavelengths. Polywave and monowave LED units were employed for this study.
Materials And Methods: Ninety bovine tooth samples were analyzed using OptiBond Universal adhesive (acetone) and single bond universal adhesive (ethanol).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!