Facile solution growth of vertically aligned ZnO nanorods sensitized with aqueous CdS and CdSe quantum dots for photovoltaic applications.

Vertically aligned single crystalline ZnO nanorod arrays, approximately 3 μm in length and 50-450 nm in diameter are grown by a simple solution approach on a Zn foil substrate. CdS and CdSe colloidal quantum dots are assembled onto ZnO nanorods array using water-soluble nanocrystals capped as-synthesized with a short-chain bifuncional linker thioglycolic acid. The solar cells co-sensitized with both CdS and CdSe quantum dots demonstrate superior efficiency compared with the cells using only one type of quantum dots. A thin Al2O3 layer deposited prior to quantum dot anchoring successfully acts as a barrier inhibiting electron recombination at the Zn/ZnO/electrolyte interface, resulting in power conversion efficiency of approximately 1% with an improved fill factor of 0.55. The in situ growth of ZnO nanorod arrays in a solution containing CdSe quantum dots provides better contact between two materials resulting in enhanced open circuit voltage.