The aim of this study was to evaluate, in vitro, the biaxial flexural strength (ISO 6872) of a feldspathic ceramic (VM7, Vita Zahnfabrik) coated with a resin cement with different thicknesses and polymerization mode. Control groups consisted in VM7 with and without acid etching with 10% hydrofluoric acid for 1 min. Experimental groups comprised VM7 etched, silanated and coated with Variolink II (Ivoclar Vivadent) cement, that was polymerized through the porcelain in light-cure and dual-cure modes, with thickness ≤150 µm or >150 µm. The specimens (n=15) were subjected to the biaxial flexural strength essay and analyzed fractographically. Parametric (Dunnet, Anova 2-way, Tukey) and non-parametric tests (Weibull) were used to evaluate results. Ceramic disks coated with resin cements of either activation modes and thicknesses exhibited higher flexural strength while the Weibull moduli did not present significant differences for a confidence interval of 95%.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4012/dmj.2010-123 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Response of Differently Structured Dental Polymer-Based Composites to Increasingly Aggressive Aging Conditions.
Nanomaterials (Basel)
January 2025
Department of Conservative Dentistry, University Hospital, Ludwig-Maximilians-University, Goethestr. 70, D-80336 Munich, Germany.
Objective: It is hypothesized that the way nano- and micro-hybrid polymer-based composites are structured and cured impacts the way they respond to aging.
Material And Methods: A polymer-ceramic interpenetrating network composite (Vita Enamic/VE), an industrially polymerized (Brillinat CriosST/BC), and an in situ light-cured composite with discrete inorganic fillers (Admira Fusion5/AF5) were selected. Specimens (308) were either cut from CAD/CAM blocks (VE/BC) or condensed and cured in white polyoxymethylene molds (AF5) and subjected to four different aging conditions ( = 22): (a) 24 h storage in distilled water at 37 °C; (b) 24 h storage in distilled water at 37 °C followed by thermal cycling for 10,000 cycles 5/55 °C (TC); (c) TC followed by storage in a 75% ethanol-water solution; and (d) TC followed by a 3-week demineralization/remineralization cycling.
Effect of Build Orientation on Mechanical and Physical Properties of Additively Manufactured Resins Using Digital Light Processing Technology in Dentistry: A Systematic Review.
J Contemp Dent Pract
September 2024
Department of Prosthodontics, Bharati Vidyapeeth (Deemed to be University) Dental College and Hospital, Sangli, Maharashtra, India, ORCID: https://orcid.org/0000-0002-6661-0931.
Aim: The aim of this systematic review was to evaluate the effect of build orientation on the mechanical and physical properties of additively manufactured resin using digital light processing (DLP).
Background: The properties of 3D-printed materials are influenced by various factors, including the type of additive manufacturing (AM) system and build orientation. There is a scarcity of literature on the effect of build orientation on the mechanical and physical properties of additively manufactured resins using DLP technology in dentistry.
Engineering performance and environmental assessment of sustainable concrete incorporating nano silica and metakaolin as cementitious materials.
Sci Rep
January 2025
School of Civil Engineering, Vellore Institute of Technology, Chennai, Tamil Nadu, 600127, India.
The carbon footprint associated with cement production, coupled with depletion of natural resources and climate change, underscores the need for sustainable alternatives. This study explores the effect of metakaolin (MK) and nano-silica (NS) on concrete's engineering performance and environmental impact. Initially, compressive, tensile, and flexural strength tests, along with durability assessments like water absorption, sorptivity, rapid chloride permeability, and resistance to acid and sulphate attacks, were conducted.
View Article and Find Full Text PDFExperimental and numerical analysis of pGFRP and wood cross-arm in latticed tower: a comprehensive study of mechanical deformation and flexural creep.
Sci Rep
January 2025
Institute of the Malay World and Civilisation (ATMA), Universiti Kebangsaan Malaysia (UKM), 43600, Bangi, Selangor, Malaysia.
The adoption of pultruded glass fibre-reinforced polymer (pGFRP) composites as a substitute for traditional wooden cross-arms in high transmission towers represents a relatively novel approach. These materials were selected for their high strength-to-weight ratio and lightweight properties. Despite various studies focusing on structures improvement, there still have a significant gap in understanding the deformation characteristics of full-scale cross-arms under actual operational loads.
View Article and Find Full Text PDFMechanical and optical properties of additively manufactured denture base resin in different colors modified with antimicrobial substances: An in vitro study.
J Prosthet Dent
January 2025
Associate Professor, Department of Restorative, Preventive and Pediatric Dentistry, School of Dental Medicine, University of Bern, Switzerland; and Adjunct Professor, Division of Restorative and Prosthetic Dentistry, The Ohio State University, Columbus, OH.
Statement Of Problem: Acrylic denture base resins are subject to colonization by oral and nonoral bacteria, contributing to the onset of denture stomatitis. However, how the addition of antimicrobial substances affects the mechanical and optical properties of additively manufactured denture base resin remains unclear.
Purpose: The purpose of this in vitro study was to investigate the surface roughness, color stainability, and flexural strength of antimicrobial-modified, additively manufactured polymethyl methacrylate (PMMA) denture base resin in tooth and gingiva colors.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!