Syntheses and crystal structures of two new bismuth hydroxyl borates containing [Bi2O2]2+ layers: Bi2O2[B3O5(OH)] and Bi2O2[BO2(OH)].

Two new bismuth hydroxyl borates, Bi(2)O(2)[B(3)O(5)(OH)] (I) and Bi(2)O(2)[BO(2)(OH)] (II), have been synthesized under hydrothermal conditions. Their structures were determined by single-crystal and powder X-ray diffraction data, respectively. Compound I crystallizes in the orthorhombic space group Pbca with the lattice constants of a = 6.0268(3) Å, b = 11.3635(6) Å, and c = 19.348(1) Å. Compound II crystallizes in the monoclinic space group Cm with the lattice constants of a = 5.4676(6) Å, b = 14.6643(5) Å, c = 3.9058(1) Å, and β = 135.587(6)°. The borate fundamental building block (FBB) in I is a three-ring unit [B(3)O(6)(OH)](4-), which connects one by one via sharing corners, forming an infinite zigzag chain along the a direction. The borate chains are further linked by hydrogen bonds, showing as a borate layer within the ab plane. The FBB in II is an isolated [BO(2)(OH)](2-) triangle, which links to two neighboring FBBs by strong hydrogen bonds, resulting in a borate chain along the a direction. Both compounds contain [Bi(2)O(2)](2+) layers, and the [Bi(2)O(2)](2+) layers combine with the corresponding borate layers alternatively, forming the whole structures. These two new bismuth borates are the first ones containing [Bi(2)O(2)](2+) layers in borates. The appearance of Bi(2)O(2)[BO(2)(OH)] (II) completes the series of compounds Bi(2)O(2)[BO(2)(OH)], Bi(2)O(2)CO(3), and Bi(2)O(2)[NO(3)(OH)] and the formation of Bi(2)O(2)[B(3)O(5)(OH)] provides another example in demonstrating the polymerization tendency of borate groups.