Objective: To determine the relative effects that phosphoric acid etching, metal brackets, composite resin adhesives, and filled resin sealants have on enamel decalcification.
Materials And Methods: One hundred and fifty teeth were randomly divided into six groups to test the effects of acid etching, brackets, and a composite resin adhesive. The right side of each tooth was sealed. The teeth were submitted to a simulated carious challenge by Streptococcus mutans in a nutritive media for 42 days. Scanning electron photomicrographs (SEMs) were used to qualitatively evaluate the tooth surfaces. DIAGNOdent laser fluorescence was used to quantify the decalcification changes that occurred.
Results: SEMs showed normal enamel on the control teeth, etching patterns on the acid-etched teeth, surface degradation on the teeth that had resin, and sealant tags on the sealed side. The untreated control group showed significantly less decalcification (P ≤ .05) than did all groups except the no etch+bracket group. The no etch+bracket group showed significantly less decalcification than did the etch+bracket, no etch+resin, and the etch+resin groups. Acid-etched teeth demonstrated significantly more decalcification (34%) than did those that were not etched. The teeth with resin showed significantly more decalcification (24%) than did those without resin. There was no significant difference between teeth that did and did not have brackets. The unsealed side of the teeth showed small amounts of--but significantly more--decalcification (5%) compared to the sealed side.
Conclusions: Acid etching and composite resin adhesives increase enamel decalcification in vitro, while brackets do not. Filled resin sealants protect the teeth from decalcification.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC8916187 | PMC |
| http://dx.doi.org/10.2319/121710-726.1 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
An innovative strategy for constructing multicore yolk-shell Si/C anodes for lithium-ion batteries.
J Colloid Interface Sci
January 2025
Key Laboratory of Green and High-end Utilization of Salt Lake Resources, Qinghai Provincial Key Laboratory of Resources and Chemistry of Salt Lakes, Qinghai Institute of Salt Lakes, Chinese Academy of Sciences, Xining, Qinghai 810008, China. Electronic address:
The yolk-shell architecture offers a promising solution to the challenges of silicon (Si) anodes in lithium-ion batteries (LIBs), particularly in addressing the significant volume changes that occur during charge and discharge cycles. However, traditional construction methods often rely on sacrificial templates and acid or alkali etching, which limits industrial applicability. In this work, we successfully constructed a silicon/carbon (Si/C) composite with a multicore yolk-shell structure using scalable spray drying technology and in-situ growth of metal-organic frameworks (MOFs) at room temperature.
View Article and Find Full Text PDFBond strength to eroded dentin as per chlorhexidine use for controlling erosive wear or interface aging: an 18-month assay.
Braz Oral Res
January 2025
Universidade de São Paulo - USP, School of Dentistry, Department of Operative Dentistry, São Paulo, SP, Brazil.
The aim of this study was to assess the effect of a chlorhexidine digluconate solution (CHX) applied as an antiproteolytic agent for controlling erosive tooth wear or as part of the adhesive treatment on long-term bond strength to eroded dentin. Dentin specimens were abraded with a 600-grit silicon carbide (SiC) paper for 1 min (sound dentin - S), subsequently treated with 2% CHX for 1 min (with excess removed, followed by a 6-hour rest), and eroded by exposure to Coca-Cola for 5 min, three times a day, for 5 days (CHX-treated and eroded dentin - CHXE), or only eroded (eroded dentin - E). The specimens were acid-etched (15 s), rinsed (30 s), dried (15 s), and rehydrated with 1.
View Article and Find Full Text PDFCytokine expression of soft tissue cells cultured with titanium discs and their respective supernatants in vitro.
Clin Oral Investig
January 2025
Department of Oral Biology, University Clinic of Dentistry, Medical University of Vienna, 1090, Vienna, Austria.
Objective: Titanium surface modifications improve osseointegration in dental and orthopedic implants. However, soft tissue cells can also reach the implant surface in immediate loading protocols. While previous research focused on osteogenic cells, the early response of soft tissue cells still needs to be better understood.
View Article and Find Full Text PDFCreating an extracellular matrix-like three-dimension structure to enhance the corrosion resistance and biological responses of titanium implants.
J Dent Sci
December 2024
Liaison Center for Innovative Dentistry, Graduate School of Dentistry, Tohoku University, Sendai, Japan.
Background/purpose: Titanium (Ti) is extensively used in dental and orthopedic implants due to its excellent mechanical properties. However, its smooth and biologically inert surface does not support the ingrowth of new bone, and Ti ions may have adverse biological effects. The purpose is to improve the corrosion resistance of titanium and create a 3D structured coating to enhance osseointegration through a very simple and fast surface treatment.
View Article and Find Full Text PDFA Two-in-One Strategy to Simultaneously Boost the Site Density and Turnover Frequency of Fe-N-C Oxygen Reduction Catalysts.
Angew Chem Int Ed Engl
January 2025
Hunan University, Chemistry and Chemical Engineering, Lushan South Road, Yuelu District, 410082, Changsha, CHINA.
Site density and turnover frequency are the two fundamental kinetic descriptors that determine the oxygen reduction activity of iron-nitrogen-carbon (Fe-N-C) catalysts. However, it remains a grand challenge to simultaneously optimize these two parameters in a single Fe-N-C catalyst. Here we show that treating a typical Fe-N-C catalyst with ammonium iodine (NH4I) vapor via a one-step chemical vapor deposition process not only increases the surface area and porosity of the catalyst (and thus enhanced exposure of active sites) via the etching effect of the in-situ released NH3, but also regulates the electronic structure of the Fe-N4 moieties by the iodine dopants incorporated into the carbon matrix.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!