Effect of side groups in polynorbornene films for transparent conductive substrates.

The imide-functionalized polynorbornene films exhibited excellent optical transparency in the visible range as well as high thermal stability over 200 degrees C. The indium tin oxide (ITO) thin films were coated on the imide-functionalized polynorbornene films at various deposition temperatures by employing radio-frequency (r.f.) planar magnetron sputtering system. The resulting ITO-coated imide-functionalized polynorbornene substrates showed good electrical and optical properties, while the figure of merit examination revealed that the present substrates are comparable to conventional ITO-glass substrates. This was confirmed from the preliminary result of organic light-emitting devices fabricated using the imide-functionalized polynorbornene substrates.