Objectives: This study was undertaken to evaluate the topographical features of enamel surface deproteinized with sodium hypochlorite (NaOCl) and etched with phosphoric acid (H3PO4) compared to phosphoric acid alone using Scanning Electron Microscopic (SEM) Analysis.
Study Design: 30 enamel blocks of 1 mm2 from ten human sound extracted permanent molars were obtained and treated as under: Group 1 (10 blocks): Enamel surface was etched with 37% H3PO4 gel for 15 seconds. Group 2 (10 blocks): Enamel surface was treated with 5.25% NaOCl for 60 seconds and then etched with 37% H3PO4 gel for 15 seconds. 10 enamel blocks were included in the control group where no treatment was carried out. The samples were subjected to SEM analysis and 5 microphotographs of each sample were obtained at 500X magnification and evaluated for the quality of etching pattern of the enamel in percentage (%) using Auto-CAD 2007 software.
Results: Mean values of etching pattern in Group 1 being 55.76% and Group 2 being 53.58%. No significant difference was observed between the two groups.
Conclusion: The use of 37% phosphoric acid for 15 seconds still remains the best method for pretreatment of enamel.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.17796/jcpd.35.2.9gw7147381836380 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effects of nanosecond‑ and microsecond‑pulse Er, Cr: YSGG laser on the morphology and pulp temperature of dentin in dental restoration debonding.
Lasers Med Sci
January 2025
Department of Stomatology, the First Medical Centre, Chinese PLA General Hospital, Beijing, 100853, China.
Objective: This study evaluated dentin morphology and pulp cavity temperature changes during nanosecond‑ and microsecond‑pulse Er, Cr: YSGG laser debonding restoration and residual adhesive.
Materials And Methods: Ten caries-free teeth had their enamel removed perpendicular to the long axis, followed by bonding of glass ceramic restorations. The samples were randomly divided into two groups and subjected to Er, Cr: YSGG laser (3 mJ, 100 Hz, 100 ns), (3 mJ, 100 Hz, 150 µs) for debonding of restoration and residual adhesive on dentin surfaces.
The Effect of Thermocycling on the Shear Bond Strength of Flash-free Brackets and Healing Dynamics of Enamel Microcracks: An Study.
J Contemp Dent Pract
September 2024
Department of Orthodontic, Faculty of Dentistry, Mansoura University, Mansoura, Egypt.
Aim: This study evaluates long-term shear bond strength (SBS) and enamel micro cracks (MCs) healing after using adhesive pre-coated brackets (APC).
Materials And Methods: A total of eighty extracted human premolar teeth were randomly divided into four experimental groups ( = 20 per group): Control group: Teeth underwent indentation but no bracket bonding; group II : Teeth were subjected to indentation without exposure to thermocycling; group III: Teeth experienced both indentation and thermocycling; group IV: No indentation was applied to the teeth; groups III and IV were further divided into two subgroups to simulate different clinical timelines: Subgroup A (n = 10): Teeth underwent 5,000 thermocycles, equivalent to six months of clinical use. Subgroup B (n = 10): Teeth were subjected to 10,000 thermocycles, representing 12 months of use.
Effect of different protocols in preventing demineralization in irradiated human enamel, in vitro study.
BMC Oral Health
January 2025
Department of Operative Dentistry, Faculty of Dentistry, Chulalongkorn University, Bangkok, Thailand.
Background: This in vitro study evaluated the efficacy of professional and home-use fluoride regimens for protecting irradiated enamel, undergoing pH cycling resembling xerostomia.
Methods: Sixty human premolar teeth were irradiated with a total dose of 70 Gy and subsequently sectioned into 3 × 3 cm enamel slabs. These slabs were randomly distributed into five groups (n = 12 per group): professional-use groups received fluoride varnish either weekly (FV1) or biweekly (FV2); home-use groups applied 5000 ppm (FT5) or 1450 ppm (FT) fluoride toothpaste; and a control group (control) received no treatment.
Analysis of heat induced changes in dental tissue for forensic application: A scanning electron microscope study.
Morphologie
January 2025
Department of Biostatistics, KS Hegde Medical Academy, Nitte (deemed to be university), Mangalore, Karnataka, India.
Introduction: In the forensic field, having accurate understanding of the macroscopic and microscopic alterations that occur in teeth when exposed to temperatures has remarkable significance. The preservation of delicate incinerated teeth is crucial in fire investigations that pertain to the temperature exposed, as well as the identification of victims. This preservation is necessary in order to conduct macroscopic and microscopic ultra-structural examinations, which provide valuable insights into the structural alterations that dental tissues undergo when exposed to low to high temperatures.
View Article and Find Full Text PDFAdvancements in nanohydroxyapatite: synthesis, biomedical applications and composite developments.
Regen Biomater
November 2024
National Engineering Research Center for Biomaterials, Sichuan University, Chengdu 610064, China.
Nanohydroxyapatite (nHA) is distinguished by its exceptional biocompatibility, bioactivity and biodegradability, qualities attributed to its similarity to the mineral component of human bone. This review discusses the synthesis techniques of nHA, highlighting how these methods shape its physicochemical attributes and, in turn, its utility in biomedical applications. The versatility of nHA is further enhanced by doping with biologically significant ions like magnesium or zinc, which can improve its bioactivity and confer therapeutic properties.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!