Purpose: To determine the effect of resin surface treatment with dissolved maleic anhydride in butanone added into primer on the tensile bond strength between an acrylic denture base resin and a silicone soft liner.
Materials And Methods: To test tensile bond strength, standard dumbbell-shaped acrylic specimens were prepared. Five experimental groups, including the control, were tested (n = 5). Maleic anhydride solutions prepared in butanone at concentrations of 1%, 5%, 10% or 20% were then mixed with 1 ml of Primo adhesive and the mixtures were applied onto the resin bonding surfaces. Silicone liner material was applied to resin surfaces in the conventional manner. Tensile bond strength of the specimens was measured in a universal testing machine. Fractured surfaces were observed under the scanning electron microscope, and resulting chemical changes with the solutions used were analyzed spectroscopically.
Results: The highest bond strength value was obtained for the group treated with 5% maleic anhydride (2.53 ± 0.48 MPa); the lowest value was for the group treated with 20% maleic anhydride (1.59 ± 0.29 MPa). Mixed failure was the dominant type seen in the experimental groups. Spectroscopic analysis showed the interaction of the anhydride carbonyl groups with the Primo primer.
Conclusion: The treatment of resin surfaces with maleic anhydride added to Primo adhesive effectively increased bond strength between silicone soft liner and denture base resin.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.a19817 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Free radical synthesis of succinic anhydride grafted poly(lactic acid) porous templates for sustained drug delivery in the buffer media.
Int J Biol Macromol
January 2025
Department of Chemistry, Suleyman Demirel University, Faculty of Arts and Science, 32260 Isparta, Turkey.
Poly(lactic) (PLA) is a biodegradable material obtained from renewable resources and is recognized as a safe biopolymer by the Food and Drug Administration. PLA expresses excellent mechanical and moldability attributes nonetheless poor elasticity/functionality limits its widespread utilization. One approach to compensate for this is chemical surface modification through free radical grafting with small organic molecules like maleic anhydride (MA).
View Article and Find Full Text PDFThiol-maleimide click reaction-driven imprinted polymer for chiral resolution of indoprofen.
J Chromatogr A
January 2025
Chemistry Department, Faculty of Science, Taibah University, Yanbu, Saudi Arabia; Chemistry Department, Faculty of Science, Mansoura University, Mansoura, Egypt. Electronic address:
Indoprofen (INP) comprises two enantiomers, R- and S-, whose high pharmacological efficacy is realized only in the case of the separated enantiomers. A newly synthesized poly(acrylonitrile-co-divinylbenzene) (PANB)-based sorbent with selective affinity to the S-enantiomer of INP was applied to separate INP racemate. The synthesis was performed by suspension polymerization with low-crosslinked PANB microparticles and by reaction of the inserted nitriles with 1-amino-1H-pyrrole-2,5‑dione (Ma-NH).
View Article and Find Full Text PDFIntermetallic RNiSi (R = Ca, La, and Y) Catalysts with Electron-Rich Ni Sites for Continuous Flow Selective Hydrogenation of Maleic Anhydride.
ACS Appl Mater Interfaces
January 2025
State Key Laboratory of Fine Chemicals, Laboratory of Advanced Materials and Catalytic Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China.
The industrial advancement of downstream products resulting from the directed hydrogenation of maleic anhydride is hindered by the limitations related to the activity and stability of catalysts. The development of nonprecious metal intermetallic compounds, in which active sites are adjustable in the local structures and electronic properties embedded within a distinct framework, holds immense potential in enhancing catalytic efficacy and stability. Herein, we report that nickel-based silicides catalysts, RNiSi (R = Ca, La, and Y), afford high efficiency in the selective hydrogenation of maleic anhydride.
View Article and Find Full Text PDFPoly(ethylene-co-(acrylic acid)) and maleic anhydride effect on micro crystalline cellulose and lignin-filled EPDM automotive sealing profiles.
Int J Biol Macromol
January 2025
Civil Engineering Department, Düzce University, Duzce, Turkey. Electronic address:
Article Synopsis
- The study examined how Poly(ethylene-co-(acrylic acid)) and maleic anhydride influence the properties of EPDM elastomers filled with cellulose and lignin.
- Adding these compounds improved thermal stability and elongation, while slowing down the vulcanization process.
- Maleic anhydride particularly enhanced tensile strength due to better chain mobility and stress transfer, making these modified elastomers beneficial for industrial applications involving biopolymers.
Polypropylene Modified with Polyethylene Through Reactive Melt Blending: Fabrication and Characterizations.
Polymers (Basel)
December 2024
Department of Chemical Engineering, Hanyang University, Ansan 15588, Republic of Korea.
Conventional PP with a linear chain structure is not suitable for foam processing due to its poor rheological properties. In this study, PP was modified with PE through reactive melt blending of maleic anhydride-grafted PP (MA-PP) with a small amount of PE bearing glycidyl groups on its backbone (G-PE), with the aim of enhancing the melt rheological properties of PP to make it suitable for foam processing. An anhydride-epoxy reaction occurred between MA-PP and G-PE during the melt processing, resulting in the formation of a crosslinked polymer network, which was confirmed by FTIR spectroscopy, a solubility test, and the presence of a rubbery plateau above the melting point.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!