The effect of different preparation and etching procedures on the microleakage of direct composite veneer restorations.

Objectives: The aim of this in vitro study was to compare the microleakage of direct composite veneer restorations prepared by a conventional dental bur or Er,Cr:YSGG (erbium, chromium doped yttrium scandium gallium garnet) laser and etched with different procedures.

Methods: Fifty maxillary incisor teeth prepared for direct veneers with gingival margins in dentin and incisal margins in enamel were randomly divided into five groups (n = 10): group 1 (control), prepared with diamond bur and etched with phosphoric acid; group 2, prepared with diamond bur and etched with Er,Cr:YSGG laser (Waterlase MD/Biolase); group 3, prepared with laser and not etched; group 4, prepared with laser and etched with phosphoric acid; and group 5, prepared and etched with laser. After the application of the etch and rinse adhesive system (Prime & Bond NT/Dentsply), teeth were restored with the nano ceramic restorative material (Ceram X Duo/Dentsply), subjected to thermocycling and immersed in 0.5% basic fuchsin dye for 24 h. The teeth were sectioned longitudinally and dye penetration was evaluated by a binocular stereomicroscope equipped with a measuring device. Data were analyzed by Kruskal-Wallis and Wilcoxon signed ranks tests. The level of significance was set at p = 0.05.

Results: Significant differences were observed in enamel of the five groups (p < 0.05). Minimal microleakage was observed in groups 1 and 3. The highest microleakage was evaluated in group 5 (p < 0.05). No significant differences were found among the five groups in dentin (p > 0.05). No differences were recorded between the microleakage values in enamel and dentin within each group and this was valid for all groups (p > 0.05).

Conclusions: The results confirmed that enamel and dentin surfaces prepared with Er,Cr:YSGG laser for direct composite veneer restorations may provide comparable sealing.