The in vivo erosion behavior of crosslinked (co)polymers based on trimethylene carbonate (TMC) and ε-caprolactone (CL) was investigated. High molecular weight poly(trimethylene carbonate) (PTMC) homopolymer- and copolymer films were crosslinked by gamma irradiation. To adjust the in vivo erosion rate of the (co)polymer films, both the irradiation dose (25, 50, or 100 kGy) for PTMC and composition (100-70 mol % TMC) at a constant irradiation dose of 25 kGy were varied. After subcutaneous implantation of irradiated films in rats, their in vivo behavior was evaluated qualitatively and quantitatively. When the irradiation dose for PTMC was increased from 25 to 100 kGy, the erosion rate of nonextracted PTMC films (determined at day 5) decreased from 39.7 ± 16.0 μm day(-1) to 15.1 ± 2.5 μm day(-1), and the number of lymphocytes in the tissue surrounding the films decreased from 235 ± 114 cells mm(-2) to 64 ± 33 cells mm(-2). The number of macrophages and giant cells at the tissue-polymer interface also decreased with increasing irradiation dose. All (co)polymer films eroded completely within 28 days of implantation. Variation of the TMC content of gamma irradiated (co)polymer films did not affect the tissue response to the gamma irradiated (co)polymer films and their in vivo erosion behavior much.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1002/jbm.a.32921 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Thermal Resistance Enhancement and Wettability Amelioration of Poly(benzimidazole-aramid) Film by Silica Nanocomposites.
Polymers (Basel)
December 2024
Graduate School of Advanced Science and Technology, Japan Advanced Institute of Science and Technology (JAIST), 1-1 Asahidai, Nomi 923-1292, Japan.
Polybenzimidazole (PBI) is a high-performance polymer known for its excellent thermal stability, mechanical strength, and chemical resistance, attributes that are derived from its unique structure comprising repeated benzene and imidazole rings. However, limitations such as relatively low thermal stability and moisture sensitivity restrict its application as a super engineering plastic. In this study, amide groups are incorporated into the PBI backbone to synthesize the copolymer poly(BI--A), effecting a structural modification at the molecular level.
View Article and Find Full Text PDFHigh-Performance Porous Supports Based on Hydroxyl-Terminated Polysulfone and CO/CO-Selective Composite Membranes.
Polymers (Basel)
December 2024
Department of Chemistry, Lomonosov Moscow State University, Leninskie Gory, 1, 119991 Moscow, Russia.
The scope of this work was to develop a thin-film composite (TFC) membrane for the separation of CO/CO mixtures, which are relevant for many processes of gas processing and gasification of carbon-based feedstock. Special attention was given to the development of highly permeable porous polysulfone (PSF) supports (more than 26,000 GPU for CO) since both the selective and support layers contribute significantly to the overall performance of the TFC membrane. The PSF porous support is widely used in commercial and lab-scale TFC membranes, and its porous structure and other exploitation parameters are set during the non-solvent-induced phase separation (NIPS) process.
View Article and Find Full Text PDFSimple A-D-A Nonfullerene Acceptors for Efficient Binary Bulk Heterojunction Organic Solar Cells.
ACS Appl Mater Interfaces
January 2025
Département de chimie, Université de Sherbrooke, Sherbrooke, Québec J1K 2R1, Canada.
Article Synopsis
- Two new nonfused ring electron acceptors were synthesized, showing a unique A-D-A (acceptor-donor-acceptor) structure and demonstrating significant absorption properties in the range of 540 nm to 700 nm.
- Their fluorescence occurs in the near-IR region, with lifetimes between 75-410 ps, and electrochemical measurements provide insights into their energy levels (HOMO and LUMO).
- The nonfused NFAs were incorporated into photovoltaic cells, achieving impressive power conversion efficiencies of 10.17% and 14.09%, indicating their potential for simpler applications in organic solar technology.
Mechanisms of alignment of lamellar-forming block copolymer under shear flow.
Soft Matter
December 2024
Departament de Física de la Matèria Condensada, Universitat de Barcelona, Martí i Franqués 1, 08028 Barcelona, Spain.
The potential applications of block copolymer thin films, utilising their self-assembly capabilities, are enhanced when achieving long-range ordering. In this study we explain the experimental alignment of lamellae under shear flow findings [S. Pujari , 2012, , 5258] and classify the alignment mechanisms based on shear rate and segregation, uncovering similarities to the systems subjected to electric fields, suggesting a common pathway of lamellae orientations.
View Article and Find Full Text PDFDynamic Covalent Bonds-Mediated Color-Switchable Circularly Polarized Luminescence in Helical Assemblies of Achiral Liquid Crystal Block Copolymer Films.
Angew Chem Int Ed Engl
December 2024
School of Chemistry and Chemical Engineering, Shanghai Key Laboratory of Electrical Insulation and Thermal Aging, Shanghai Jiao Tong University, Dongchuan Road no. 800, Shanghai, 200240, China.
Circularly polarized luminescence (CPL) film attracted considerable attention in information storage and encryption, three-dimensional display, and chiral recognition. However, due to the limited molecular mobility within thin film, achieving a high asymmetry factor and non-contact modulation of CPL remain challenging. In this work, color-switchable homochiral CPL films with high luminescence asymmetry factor (g~0.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!