Purpose: This study evaluated the effect of pattern coating with spinel-based investment Rematitan Ultra (RU) on the castability and internal porosity of commercially pure (CP) titanium invested into phosphate-bonded investments. The apparent porosity of the investment was also measured.
Materials And Methods: Square patterns (15 × 15 × 0.3 mm(3)) were either coated with RU, or not and invested into the phosphate-bonded investments: Rematitan Plus (RP), Rema Exakt (RE), Castorit Super C (CA), and RU (control group). The castings were made in an Ar-arc vacuum-pressure machine. The castability area (mm(2) ) was measured by an image-analysis system (n = 10). For internal porosity, the casting (12 × 12 × 2 mm(3) ) was studied by the X-ray method, and the projected porous area percentage was measured by an image-analysis system (n = 10). The apparent porosity of the investment (n = 10) was measured in accordance with the ASTM C373-88 standard.
Results: Analysis of variance (One-way ANOVA) of castability was significant, and the Tukey test indicated that RU had the highest mean but the investing technique with coating increased the castability for all phosphate-bonded investments. The analysis of the internal porosity of the cast by the nonparametric test demonstrated that the RP, RE, and CA with coating and RP without coating did not differ from the control group (RU), while the CA and RE casts without coating were more porous. The one-way ANOVA of apparent porosity of the investment was significant, and the Tukey test showed that the means of RU (36.10%) and CA (37.22%) were higher than those of RP (25.91%) and RE (26.02%).
Conclusion: Pattern coating with spinel-based material prior to phosphate-bonded investments can influence the castability and the internal porosity of CP Ti.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1111/j.1532-849X.2010.00629.x | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
A Lab-Based Study to Assess the Surface Roughness of Various Investments: An Original Research.
J Pharm Bioallied Sci
February 2024
BDS, Intern, Kalinga Institute of Dental Sciences, Kalinga Institute of Industrial Technology (KIIT) Deemed to be University, Bhubaneswar, Odisha, India.
Introduction: Surface roughness of the crowns is dependent on the pattern material used for the making as well as the procedure of investing. The study was aimed to examine the impact of various pattern materials and investment procedures on the surface roughness of nickel-chromium alloy raw castings.
Materials And Methods: An study was piloted at a tertiary care hospital.
Synthesis of β-tricalcium phosphate by modifying the heating process of a dental casting mold.
Dent Mater J
September 2023
Department of Oral Implantology, Division of Oral Pathogenesis and Disease Control, Asahi University School of Dentistry.
This study investigated a novel method for artificial synthesis of β-tricalcium phosphate (β-TCP). The binder of the phosphate-bonded investment was replaced with calcium oxide instead of magnesium oxide and sintered in an electric furnace. The water/powder mixing ratio for hardening was determined using preliminary experiments.
View Article and Find Full Text PDFAnalyse the effect of different investment techniques and pattern materials on surface roughness of raw Ni-Cr castings - An study.
J Indian Prosthodont Soc
January 2020
Department of Prosthodontics and Implantology, Bharati Vidyapeeth Dental College and Hospital, Sangli, Maharashtra, India.
Aims: This study aimed to analyze the effect of different investment techniques and pattern materials on the surface roughness of raw castings from nickel-chromium alloy.
Settings And Design: This is an experimental in vitro study carried out in Bharati Vidyapeeth Dental College and Hospital, Sangli, Maharastra.
Materials And Methods: Sixty square-shaped wax patterns, measuring 10 mm × 10 mm × 2 mm, were divided into four groups.
Comparative evaluation of diametral tensile strength of phosphate-bonded investment (ringless) material by using air-drying method, conventional hot air oven, microwave oven, and combination of microwave and conventional oven: An study.
J Indian Prosthodont Soc
January 2019
Department of Prosthodontics, V.S.P.M's Dental College and Research Centre, Nagpur, Maharashtra, India.
Aim: This study evaluated and compared the diametral tensile strength (DTS) of phosphate-bonded investment (PBI) material (ringless) used in removable cast partial denture fabrication.
Settings And Design: Comparative - study.
Materials And Methods: The PBI material, Wirovest used in this study was subjected to four different drying methods.
The Effect of Casting Ring Liner Length and Prewetting on the Marginal Adaptation and Dimensional Accuracy of Full Crown Castings.
J Int Soc Prev Community Dent
February 2017
Department of Prosthodontics, College of Dentistry, King Khalid University, Abha, Saudi Arabia.
Aim: To evaluate the effect of varying cellulose casting ring liner length and its prewetting on the marginal adaptation and dimensional accuracy of full veneer metal castings.
Materials And Methods: The master die was milled in stainless steel to fabricate the wax pattern. Sixty wax patterns were fabricated with a uniform thickness of 1.