Objectives: To verify the effect of interposing different indirect restorative materials on degree of conversion (DC), hardness, and flexural strength of a dual-cure resin cement.
Methods: Discs (2 mm-thick, n=5) of four indirect restorative materials were manufactured: a layered glass-ceramic (GC); a heat-pressed lithium disilicate-based glass-ceramic veneered with the layered glass-ceramic (LD); a micro-hybrid (MH); and a micro-filled (MF) indirect composite resin. The light transmittance of these materials was determined using a double-beam spectrophotometer with an integrating sphere. Bar-shaped specimens of a dual-cure resin cement (Nexus 2/SDS Kerr), with (dual-cure mode) and without the catalyst paste (light-cure mode), were photoactivated through the discs using either a quartz-tungsten-halogen (QTH) or a light-emitting diode (LED) unit. As a control, specimens were photoactivated without the interposed discs. Specimens were stored at 37 masculineC for 24h before being submitted to FT-Raman spectrometry (n=3), Knoop microhardness (n=6) and three-point bending (n=6) tests. Data were analyzed by ANOVA/Tukey's test (alpha=0.05).
Results: MH presented the highest transmittance. The DC was lower in light-cure mode than in dual-cure mode. All restorative materials reduced the cement microhardness in light-cure mode. GC and LD with QTH and GC with LED decreased the strength of the cement for both activation modes compared to the controls. Curing units did not affect DC or microhardness, except when the dual-cure cement was photoactivated through LD (LED>QTH). Flexural strength was higher with QTH compared to LED.
Conclusions: Differences in transmittance among the restorative materials significantly influenced cement DC and flexural strength, regardless of the activation mode, as well as the microhardness of the resin cement tested in light-cure mode. Microhardness was not impaired by the interposed materials when the resin cement was used in dual-cure mode.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC2897866 | PMC |
Publication Analysis
Top Keywords
Similar Publications
TRPV4 as a Novel Regulator of Ferroptosis in Colon Adenocarcinoma: Implications for Prognosis and Therapeutic Targeting.
Dig Dis Sci
January 2025
Ningxia Medical University, Xing Qing Block, Shengli Street No.1160, Yin Chuan City, 750004, Ningxia Province, People's Republic of China.
Background: Colon adenocarcinoma (COAD) is a leading cause of cancer-related mortality worldwide. Transient receptor potential vanilloid 4 (TRPV4), a calcium-permeable non-selective cation channel, has been implicated in various cancers, including COAD. This study investigates the role of TRPV4 in colon adenocarcinoma and elucidates its potential mechanism via the ferroptosis pathway.
View Article and Find Full Text PDFNew Numerical Inversion Method to Improve the Spatial Accuracy of Elemental Imaging for LA-ICP-MS.
Anal Chem
January 2025
State Key Laboratory of Geological Processes and Mineral Resources, China University of Geosciences, Wuhan 430074, PR China.
The elemental imaging of laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) provides spatial information on elements and therefore can further investigate the growth or evolution processes of an analyte. However, the accurate determination of spatial information is limited by the decoupling between the elemental distribution and mass spectrometry signals. This phenomenon, which is more distinct when high-diffusion ablation cells are used, arises from the overlap of ablation and the transport dispersion of aerosols.
View Article and Find Full Text PDFEffect of Cervical Margin Relocation With Different Injectable Restorative Materials on Fracture Resistance of Molars Received MOD CAD/CAM Onlay Restorations.
J Esthet Restor Dent
January 2025
Operative Department, Faculty of Dentistry, Mansoura University, Mansoura, Egypt.
Objective: To investigate the effect of cervical margin relocation with four different injectable restorative materials on the fracture resistance of molars receiving mesio-occluso-distal CAD/CAM nanoceramic onlay restorations.
Materials And Methods: One hundred and five sound mandibular molars received a standardized mesio-occluso-distal onlay preparation, with cervical margins located 2 mm apical to the cemento-enamel junction. The molars were randomly allocated into five groups (n = 21) according to the cervical relocating materials used: Group I had no cervical margin relocation; Group II used a highly viscous glass ionomer; Group III used a highly-filled injectable resin composite; Group IV used a resin-modified glass ionomer; and Group V used a bioactive ionic resin.
The Effect of Polyethylene Fiber and Flowable Resin Composite on Fracture Resistance in the Restoration of Large MOD Cavities.
J Esthet Restor Dent
January 2025
Department of Restorative Dentistry, Faculty of Dentistry, Kırıkkale University, Kırıkkale, Türkiye.
Objective: This in vitro study aims to evaluate the effect of placing polyethylene fibers used in large Class II MOD (mesio-occlusion-distal) cavities into different flowable resin composites and in different positions on the fracture resistance of the restoration.
Materials And Methods: Ninety healthy human molars were used in the study. No treatment was performed on 10 of these teeth and they were used as the control group.
Effect of In Situ Acid Erosion on Structural and Optical Properties of Nanoparticulated Bisacrylic Resin With Different Surface Treatments.
J Esthet Restor Dent
January 2025
Department of Dental Materials and Prosthodontics, Sao Paulo State University (UNESP), School of Dentistry, Araçatuba, São Paulo, Brazil.
Objective: To evaluate the influence of in situ acid erosion on the structural and optical properties of nanoparticulate bisacrylic resin with different surface treatments, evaluating surface roughness (Ra), knoop microhardness (KHN), color change (ΔE, ΔL, ΔC, ΔH), contrast (CR) and translucency (TP).
Methods: Eighty specimens were made (n = 10 per group) and the following surface treatments were applied: U-unpolished; A-polishing with Astropol rubber tips (Ivoclar); S-Biscover LV surface sealant (Bisco) and S-Palaseal surface sealant (kulzer). For the in situ experiment, 10 volunteers wore an intraoral appliance containing eight specimens (two specimens per experimental group), with only one specimen from each experimental group being subjected to the acid process.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!