The reactivity of the redox-active tetracarboxylic acid derived from the tetrathiafulvalene (TTF-TC)H(4) with alkaline cations (K, Rb, Cs) is reported. The exploration of various experimental parameters (temperature, pH) led to the formation of four crystalline three-dimensional coordination polymers formulated M(2)(TTF-TC)H(2) (M = K, Rb, Cs), denoted MIL-132(K), MIL-133(isostructural K, Rb), and MIL-134(Cs). Thermogravimetric analysis and thermodiffraction show that all of the solids are thermally stable up to 150-200 degrees C in the air. In order to exploit the possibility of oxidation of the organic linker in TTF-based compounds, they were employed as positive electrodes in a classical lithium cell. A highly reversible cyclability was achieved at high current density (10 C) with a reasonable performance (approximately 50 mAh g(-1)). Finally, combined electro-(sub)hydrothermal synthesis was used to prepare a fifth 3-D coordination polymer formulated K(TTF-TC)H(2) (denoted MIL-135(K)), this time not based on the neutral TTF-TC linker but its radical, oxidized form TTF-TC(+*). This solid is less thermally stable than its neutral counterparts but exhibits a semiconducting behavior, with a conductivity at room temperature of about 1 mS cm(-1).

Download full-text PDF

Source
http://dx.doi.org/10.1021/ic100950nDOI Listing

Publication Analysis

Top Keywords

3-d coordination
8
coordination polymers
8
thermally stable
8
polymers based
4
based tetrathiafulvalenetetracarboxylate
4
tetrathiafulvalenetetracarboxylate ttf-tc
4
ttf-tc derivative
4
derivative synthesis
4
synthesis characterization
4
characterization oxidation
4

Similar Publications

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!