Shear strength of the bond to primary dentin: influence of Er:YAG laser irradiation distance.

Lasers Med Sci

Department of Pediatric Clinics, Preventive and Social Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo, Av. do Café, S/N, Monte Alegre, CEP: 14040-904, Ribeirão Preto, SP, Brasil.

Published: May 2011

The aim of this study was to assess in vitro the influence of Er:YAG laser irradiation distance on the shear strength of the bond between an adhesive restorative system and primary dentin. A total of 60 crowns of primary molars were embedded in acrylic resin and mechanically ground to expose a flat dentin surface and were randomly assigned to six groups (n = 10). The control group was etched with 37% phosphoric acid. The remaining five groups were irradiated (80 mJ, 2 Hz) at different irradiation distances (11, 12, 16, 17 and 20 mm), followed by acid etching. An adhesive agent (Single Bond) was applied to the bonding sites, and resin cylinders (Filtek Z250) were prepared. The shear bond strength tests were performed in a universal testing machine (0.5 mm/min). Data were submitted to statistical analysis using one-way ANOVA and the Kruskal-Wallis test (p<0.05). The mean shear bond strengths were: 7.32 ± 3.83, 5.07 ± 2.62, 6.49 ± 1.64, 7.71 ± 0.66, 7.33 ± 0.02, and 9.65 ± 2.41 MPa in the control group and the groups irradiated at 11, 12, 16, 17, and 20 mm, respectively. The differences between the bond strengths in groups II and IV and between the bond strengths in groups II and VI were statistically significant (p<0.05). Increasing the laser irradiation distance resulted in increasing shear strength of the bond to primary dentin.

Download full-text PDF

Source
http://dx.doi.org/10.1007/s10103-010-0776-yDOI Listing

Publication Analysis

Top Keywords

shear strength
8
strength bond
8
primary dentin
8
influence eryag
8
eryag laser
8
laser irradiation
8
irradiation distance
8
bond
4
bond primary
4
dentin influence
4

Similar Publications

Aim: The aim of this systematic review was to evaluate the effect of build orientation on the mechanical and physical properties of additively manufactured resin using digital light processing (DLP).

Background: The properties of 3D-printed materials are influenced by various factors, including the type of additive manufacturing (AM) system and build orientation. There is a scarcity of literature on the effect of build orientation on the mechanical and physical properties of additively manufactured resins using DLP technology in dentistry.

View Article and Find Full Text PDF

Shear Strength of Adhesives Based on Solvent Type, Aged, and LED-cured with Different Wavelengths: An Study.

J Contemp Dent Pract

September 2024

Department of Academic, Faculty of Dentistry, Universidad Nacional Federico Villarreal, Lima, Peru, ORCID: https://orcid.org/0000-0002-0594-5834.

Objective: To evaluate the shear strength of adhesives based on the type of solvent (ethanol and acetone), aged and light-cured using light-emitting diode (LED) units with different wavelengths. Polywave and monowave LED units were employed for this study.

Materials And Methods: Ninety bovine tooth samples were analyzed using OptiBond Universal adhesive (acetone) and single bond universal adhesive (ethanol).

View Article and Find Full Text PDF

Aim: This study evaluates long-term shear bond strength (SBS) and enamel micro cracks (MCs) healing after using adhesive pre-coated brackets (APC).

Materials And Methods: A total of eighty extracted human premolar teeth were randomly divided into four experimental groups ( = 20 per group): Control group: Teeth underwent indentation but no bracket bonding; group II : Teeth were subjected to indentation without exposure to thermocycling; group III: Teeth experienced both indentation and thermocycling; group IV: No indentation was applied to the teeth; groups III and IV were further divided into two subgroups to simulate different clinical timelines: Subgroup A (n = 10): Teeth underwent 5,000 thermocycles, equivalent to six months of clinical use. Subgroup B (n = 10): Teeth were subjected to 10,000 thermocycles, representing 12 months of use.

View Article and Find Full Text PDF

The Inner Mongolia section of the Yellow River is a seasonal frozen soil area, where the freeze-thaw effect can alter soil strength and compressibility, affecting bank stability. This study takes the banks sandy silt of the Inner Mongolia section of the Yellow River as the research object. It systematically investigates the relationship between shear strength parameters and compression index of sandy silt and the initial dry density, water content, and freeze-thaw cycles of the soil.

View Article and Find Full Text PDF

Microwave welding with SiCNW/PMMA nanocomposite thin films: Enhanced joint strength and performance.

Nanotechnology

January 2025

Universiti Teknologi PETRONAS, Centre of Innovative Nanostructures and Nanodevices (COINN), Universiti Teknologi PETRONAS, 32610 Seri Iskandar, Perak Darul Ridzuan, MALAYSIA, Seri Iskandar, Perak, 32610, MALAYSIA.

Most previously reported susceptors for microwave welding are in powder form. In this study, a thin-film susceptor was employed due to its uniform heating rate and ease of handling. Silicon carbide nanowhisker (SiCNW) were incorporated into a poly(methyl methacrylate) (PMMA) matrix to create a nanocomposite thin film, which served as the susceptor.

View Article and Find Full Text PDF

Want AI Summaries of new PubMed Abstracts delivered to your In-box?

Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!