Objective: To investigate the structure, mechanical and low temperature aging properties of colored dental zirconia ceramics.
Methods: 5 graded colored dental zirconia ceramics were made by adding colorants and their combinations into a 3Y-TZP (tetragonal zirconia stabilized by 3mol% yttrium) powder, the green body were compacted at 200 MPa, pre-sinter at 1,050 degrees C and maintained for 2 h, then densely sintered at 1,500 degrees C for 2 h. Specimens were cut from each of the 5 graded colored blocks. Physical, mechanical properties as well as chemical stability were tested, microstructure were observed, crystalline phase were identified by X-ray diffraction (XRD), aging properties were assessed by measurement of the relative content of monoclinic phase and bending strength testing.
Results: The overall density of colored zirconia ceramics was over 99.7%, linear shrinkage was about 20%, while thermal expansion coefficient was about 11 x 10(-6) x degrees C(-1), the crystalline phase was tetragonal, bending strength was over 900 MPa which was slightly lowered than that of the uncolored zirconia, fracture toughness was slightly higher. Good chemical stability in acetic acid was observed. After aging treatment, tetragonal-to-monoclinic phase transformation was detected up to 40%, while bending strength was not significantly degraded.
Conclusion: The results showed that colored 3Y-TZP ceramics presented good mechanical properties even after aging treatments, and was suitable for dental clinical use.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Comparative color stability assessment of orthodontic clear aligners: an in vitro study.
Sci Rep
January 2025
Dental Students, College of Medicine and Dentistry, Riyadh Elm University, Riyadh, KSA, Saudi Arabia.
Objective To evaluate the stain resistance and color stability of four Clear aligners (CA) brands against various beverages at different intervals, along with assessing the elaboration of cleaning agents. Methods In a strictly controlled lab environment, 48 CAs from four different companies (Invisalign, EON, Clear Cap, and K clear) were immersed for seven days in six different beverages based on their pH (Pepsi, orange juice, milk, coffee, and black tea), as well as a control solution (distilled water). The VITA Easy-Shade compact colorimeter used the Commission International lightening L*a*b* color scheme to evaluate the color change of the aligners at four intervals.
View Article and Find Full Text PDFVitamin C mesotherapy with microneedling for gingival depigmentation: A case study.
Clin Adv Periodontics
January 2025
Department of Biostatistics, All India Institute of Medical Sciences, New Delhi, India.
Background: Surgical methods of gingival depigmentation can be challenging, particularly if the gingival phenotype is thin due to the risk of gingival recession and bone exposure. Thus, exploring alternative, non-surgical, minimally invasive treatment modalities is warranted. In dermatology, vitamin C is extensively used for depigmentation and microneedling for collagen induction, with limited literature about its usage for improving gingival esthetics.
View Article and Find Full Text PDFImpact of Different Time Intervals on the Color Stability of Glass Ionomer Cement and Composite Materials Bonded to Silver Diamine Fluoride: An In Vitro Study.
Cureus
December 2024
Pedodontics and Preventive Dentistry, SRM Kattankulathur Dental College, Chennai, IND.
Objective This in vitro study evaluated the impact of different time intervals on the color stability of glass ionomer cement (GIC) and composite materials bonded to teeth treated with silver diamine fluoride (SDF). Specifically, the study sought to determine if immediate or delayed application of these restorative materials affects the degree of staining caused by SDF. Materials and methods Twenty-eight extracted primary molars with cavitated lesions were randomly divided into four groups, each comprising seven samples.
View Article and Find Full Text PDFBackground: It is generally accepted that the greater palatine nerve and artery supply the palatal mucosa, gingiva, and glands, but not the bone or tooth adjacent to those tissues. When the bony palate is observed closely, multiple small foramina are seen on the palatal surface of the alveolar process. The authors hypothesized that the greater palatine nerve and artery might supply the maxillary teeth via the foramina on the palatal surface of the alveolar process and the superior alveolar nerve and artery.
View Article and Find Full Text PDFIn vitro analysis of composition profiles of resins for 3D printing of dentures.
J Dent
January 2025
Clinic of General-, Special Care- and Geriatric Dentistry, Center for Dental Medicine, University of Zurich, Zurich, Switzerland. Electronic address:
Objective: This study aimed to investigate the resin compounds from CAD-CAM 3D-printed denture resins, focusing on the identification and classification of free monomers and other components. The primary objective was to determine the chemical profile of these 3D-prinding resin materials.
Methods: Four 3D-printed denture resins, two base materials (1: DentaBASE, Asiga Ltd.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!