Objective: To construct four different micro- and nano-phase titanium film models and investigate the characteristics of their surface micro-topography.
Methods: Four different titanium films were prepared on commercial titanium discs, by direct current magnetron sputtering, at ambient, 100, 250, 380 degrees C substrate temperature, respectively. Their surface topography and crystal sizes were investigated using atomic force microscope (AFM) and X-ray diffraction (XRD). The size of granule and surface roughness in different group was calculated and compared.
Results: All samples were covered by a thin film consisting of dense round or ovaloid granules. The granules and crystals was growing as the substrate temperature increasing. The Ti substrate had greater effect on the surface topography of film compared with Si substrate. This kind of complex topography caused the surface roughness of Ti substrate group decreased as the granules growing.
Conclusion: In our study, four different micro- and nano-phase titanium film models were constructed for our coming investigation of their topographical influence on biological reaction of proteins and cells. Basic data on surface features was obtained for next in vitro and in vivo experiment.
Download full-text PDF |
Source |
|---|
Publication Analysis
Top Keywords
Similar Publications
Effect of Ni and Nb Elements on Corrosion Resistance and Behavior of TC4 Alloy in Hydrochloric Acid.
Materials (Basel)
January 2025
GRIMAT Engineering Institute Company Limited, Beijing 101407, China.
Due to the development of the petroleum industry, more severe mining conditions put forward higher corrosion resistance requirements for materials. In this paper, the corrosion resistance and corrosion behavior of four TC4-xNi-yNb (x, y = 0, 0.5) alloys were investigated in a 1 mol/L HCl solution through microscopic characterization, electrochemical tests and corrosion weight loss testing.
View Article and Find Full Text PDFHigh-Performance Hydrogen Sensing at Room Temperature via Nb-Doped Titanium Oxide Thin Films Fabricated by Micro-Arc Oxidation.
Nanomaterials (Basel)
January 2025
Guangdong Key Laboratory of Materials and Equipment in Harsh Marine Environment, School of Ocean Engineering, Guangzhou Maritime University, Guangzhou 510725, China.
Metal oxide semiconductor (MOS) hydrogen sensors offer advantages, such as high sensitivity and fast response, but their challenges remain in achieving low-cost fabrication and stable operation at room temperature. This study investigates Nb-doped TiO (NTO) thin films prepared via a one-step micro-arc oxidation (MAO) with the addition of NbO nanoparticles into the electrolyte for room-temperature hydrogen sensing. The characterization results revealed that the incorporation of NbO altered the film's morphology and phase composition, increasing the Nb content and forming a homogeneous composite thin film.
View Article and Find Full Text PDFAn In Vivo Biostability Evaluation of ALD and Parylene-ALD Multilayers as Micro-Packaging Solutions for Small Single-Chip Implants.
Small
January 2025
Department of Microelectronics, Faculty of Electrical Engineering, Mathematics and Computer Science, Delft University of Technology, Delft, 2628 CN, The Netherlands.
Miniaturization of next-generation active neural implants requires novel micro-packaging solutions that can maintain their long-term coating performance in the body. This work presents two thin-film coatings and evaluates their biostability and in vivo performance over a 7-month animal study. To evaluate the coatings on representative surfaces, two silicon microchips with different surface microtopography are used.
View Article and Find Full Text PDF"Nano-In-Nano" Schottky Diodes Fabricated by Combining Self-Aligned Nanogap Patterning with Bottom-Up ZnO Nanowire Growth.
ACS Appl Electron Mater
January 2025
Electrical Engineering Division, Engineering Department, University of Cambridge, Cambridge CB3 0FA, U.K.
Nanoscale semiconductors offer significant advantages over their bulk semiconductor equivalents for electronic devices as a result of the ability to geometrically tune electronic properties, the absence of internal grain boundaries, and the very low absolute number of defects that are present in such small volumes of material. However, these advantages can only be realized if reliable contacts can be made to the nanoscale semiconductor using a scalable, low-cost process. Although there are many low-cost "bottom-up" techniques for directly growing nanomaterials, the fabrication of contacts at the nanoscale usually requires expensive and slow techniques like e-beam lithography that are also hard to scale to a level of throughput that is required for commercialization.
View Article and Find Full Text PDFThis paper explores the process of forming arrays of vertically oriented carbon nanotubes (CNTs) localized on metal electrodes using thin porous anodic alumina (PAA) on a solid substrate. On a silicon substrate, a titanium film served as the electrode layer, and an aluminium film served as the base layer in the initial film structure. A PAA template was formed from the Al film using two-step electrochemical anodizing.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!