This study evaluated the Knoop hardness of a dual-cured resin cement (Rely-X ARC) activated solely by chemical reaction (control group) or by chemical / physical mode, light-cured through a 1.5 mm thick ceramic (HeraCeram) or composite (Artglass) disc. Light curing was carried out using conventional halogen light (XL2500) for 40 s (QTH); light emitting diodes (Ultrablue Is) for 40 s (LED); and Xenon plasma arc (Apollo 95E) for 3 s (PAC). Bovine incisors had their buccal face flattened and hybridized. On this surface a rubber mold (5 mm in diameter and 1 mm in height) was bulk filled with the resin cement. A polyester strip was seated for direct light curing or through the discs of veneering materials. After dry storage in the dark (24 h 37 degrees C), the samples (n = 5) were sectioned for hardness (KHN) measurements, taken in a microhardness tester (50 gF load 15 s). The data were statistically analyzed by ANOVA and Tukey's test (alpha = 0.05). The cement presented higher Knoop hardness values with Artglass for QTH and LED, compared to HeraCeram. The control group and the PAC/Artglass group showed lower hardness values compared to the groups light-cured with QTH and LED. PAC/HeraCeram resulted in the worst combination for cement hardness values.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1590/s1806-83242009000200003 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Development of Composite Semiconductor Films Based on Organotin Complexes Doped with Cobalt Porphine for Applications in Organic Diodes.
Materials (Basel)
December 2024
Chemistry Institute, Universidad Nacional Autónoma de México, Circuito Exterior S/N, Ciudad Universitaria, Ciudad de México 04510, Mexico.
In this work, we present the green synthesis of complex - derived from β-hidroxymethylidene indanones by ultrasound, which allowed for the obtaining of compounds in a shorter time and with good yields. These organotin complexes were then doped with cobalt porphine and incorporated into a poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) matrix to manufacture composite semiconductor films. The semiconductor films were characterized through atomic force microscopy, examining their topography, Knoop hardness (around 17 HK), and tensile strength, which varied from 5 × 10 to 7 × 10 Pa.
View Article and Find Full Text PDFPrinted versus heat-polymerized resin for occlusal devices: Evaluation of physical and mechanical properties after brushing and microbial adhesion.
J Prosthodont
January 2025
Department of Dental Materials and Prosthesis, Ribeirão Preto Dental School, University of São Paulo (USP), Ribeirão Preto, Brazil.
Purpose: To evaluate the physical and mechanical properties after brushing and microbial adhesion of printed resins (PRs) and heat-polymerized resins (HRs) for occlusal devices (ODs).
Materials And Methods: Knoop microhardness and roughness were evaluated in three measurements before and after brushing with detergent or dentifrice. Flexural strength and modulus of elasticity were assessed by 3-point bending, and the adhesion of Candida albicans and Streptococcus mutans was evaluated by colony-forming units per milliliter (CFU/mL) and metabolic activity using the XTT assay only without brushing.
Remineralisation of enamel erosive lesions by daily-use fluoride treatments: network meta-analysis of an in situ study set.
Clin Oral Investig
December 2024
Oral Health Research Institute, Indiana University School of Dentistry, 415 Lansing Street, Indianapolis, IN, 46202-2876, USA.
Objectives: Daily-use fluoride products are first-line protection against enamel wear from dietary-acid exposure (DAE). This study aimed to understand effects of fluoride concentration, fluoride salt, product form and ingredients in daily-use products on remineralisation and demineralisation, via network meta-analysis (NMA) of 14 studies using one well-established in-situ model. Remineralisation (surface-microhardness recovery, SHMR) after treatment, and protection against subsequent demineralisation (acid-resistance ratio, ARR) were measured.
View Article and Find Full Text PDF3D-printed denture base resins: Glazing as an alternative to improve surface, mechanical, and microbiological properties.
J Prosthodont
December 2024
Department of Dentistry, Federal University of Rio Grande do Norte (UFRN), Natal, Rio Grande do Norte, Brazil.
Purpose: To evaluate the impact of glazing denture base resins (heat-polymerized and 3D-printed) on surface, mechanical, and microbiological properties.
Materials And Methods: Discs (10 × 3 mm) and bars (64 × 10 × 3.3 ± 0.
Antimicrobial activity of PMMA enriched with nano-clay loaded with metronidazole and chlorhexidine.
Braz Oral Res
December 2024
University of Saskatchewan, College of Dentistry, Saskatchewan, Canada.
Article Synopsis
- PMMA materials are prone to microbial growth, leading to potential oral infections in patients, which prompted a study using montmorillonite clay (MMT) combined with antimicrobial agents like chlorhexidine (CHX) and metronidazole (MET) to improve resistance.
- The researchers created three groups of PMMA samples—control (no nanoparticles), MMT/CHX, and MMT/MET—and tested their mechanical properties and antimicrobial effectiveness against bacteria such as Enterococcus faecalis and Porphyromonas gingivalis.
- Results showed that MMT/CHX maintained PMMA’s mechanical strength while exhibiting antibacterial properties, whereas MMT/MET negatively impacted strength, leading to the conclusion that MMT/CHX is the
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!