Unlabelled: To evaluate bond strengths of different resin cements to two aluminum oxide-based ceramics.
Methods: One hundred ten ceramic cylinders were produced and given four different surface treatments. Resin cement cylinders were then bonded to the ceramic cylinders using different resin cements and the bond strength was determined by shear testing to the breaking point. We were thus able to obtain results for the different combinations of porcelain, surface treatments and cements. All data was analyzed using the Kruskal-Wallis test for more than two independent samples and the Bonferroni correction applied (a=0.01). An optical microscopy study was carried out to analyze the type of failure, and an electronic microscopy examination was carried out in order to evaluate the changes produced in the ceramic by the different surface treatments.
Results: The best values corresponded to the control group, composed of silicate ceramics combined with Variolink II resin cement. In-Ceram Alumina showed no significant differences with respect to the type of cement applied. Procera AllCeram obtained the best values when silica coated using the CoJet System and applying Variolink II, or when sandblasted and applying Clearfil SE Bond + Porcelain Bond Activator and Panavia F cement.
Significance: Surface treatment modifies the ceramic surface and influences the bond strength, as does the type of cement used. Silica coating is recommended to improve adhesion to Procera AllCeram, applying Variolink II, or sandblasting plus resin cement containing MDP (Panavia F).
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4317/medoral.15.e95 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Evaluation of bond durability of different self-adhesive bioactive restorative systems to dentin.
Sci Rep
January 2025
Conservative Dentistry Department, Faculty of Dentistry, Mansoura University, Mansoura, Egypt.
This study aimed to compare the bonding efficacy three bioactive self-adhesive restorative systems to dentin. A total of 80 permanent human molars were utilized in this study. The occlusal enamel was removed to exposed mid-coronal dentin; 40 molars were used for microshear bond strength testing, while the remaining molars were used for micromorphological analysis of restoration/dentin interface.
View Article and Find Full Text PDFIn vitro evaluation of antimicrobial photodynamic therapy with photosensitizers and calcium hydroxide on bond strength, chemical composition, and sealing of glass-fiber posts to root dentin.
Lasers Med Sci
January 2025
Department of Preventive and Restorative Dentistry, Discipline of Endodontics, Araçatuba School of Dentistry, São Paulo State University - UNESP, Araçatuba, SP, Brazil.
Investigate the impact of antimicrobial photodynamic therapy (aPDT) using different photosensitizers (PSs) such as indocyanine green (IG), curcumin (CC), and methylene blue (MB), with or without intracanal application of calcium hydroxide (CH), on the push-out bond strength of glass-fiber posts (GFPs) to intraradicular dentin, the chemical composition of the root substrate, and the sealing of the adhesive interface across different thirds of intraradicular dentin. A total of 112 bovine teeth underwent biomechanical preparation and were divided into eight experimental groups (n = 14 each): Negative control with deionized water; positive control with deionized water + CH; IG group with indocyanine green and infrared laser; IG + CH group; CC group with curcumin and blue LED; CC + CH group; MB group with methylene blue and red laser; and MB + CH group. The push-out bond strength was measured using a universal testing machine (n = 8), and scanning electron microscopy characterized the fracture patterns.
View Article and Find Full Text PDFInfluence of dual-cure resin-cement curing modes on gingival cytotoxicity and inflammatory responses.
J Dent Sci
January 2025
Division of Molecular & Regenerative Prosthodontics, Tohoku University Graduate School of Dentistry, Sendai, Japan.
Background/purpose: Dual-cure resin-cements are used for various dental restorations. However, whether the curing modes of these resin-cements influence gingival inflammation remains unclear. Hence, herein, we evaluated the effects of dual-cure resin-cement curing modes on gingival cytotoxicity and inflammatory responses.
View Article and Find Full Text PDFANTIMICROBIAL ACTION OF A MODIFIED UNIVERSAL ADHESIVE: AN IN VITRO STUDY.
Georgian Med News
November 2024
2Department of Conservative Dentistry, College of Dentistry, University of Mosul, Iraq.
Background: Resin composites and dental adhesives are widely used to restore carious teeth. A relatively new category of the dental adhesives, the universal adhesives (UAs) is considered user friendly because of its simplicity to use and compatibility with any adhesive strategy. However, the adhesive interface created by these adhesives is highly susceptible to cracking after polymerization which in turn facilitates the initiation of secondary caries.
View Article and Find Full Text PDFWear Resistance of Light-Cure Resin Luting Cements for Ceramic Veneers.
J Funct Biomater
December 2024
Department of Operative Dentistry, School of Dentistry, Aichi Gakuin University, Nagoya 464-8651, Japan.
The purpose of this study was to compare the wear resistance of light-cure resin luting cements for veneers with that of other luting materials investigated in earlier studies. An Alabama wear-testing machine was used to measure the wear resistance of four recent light-cure resin luting cements for veneers (G-Cem Veneer; Panavia V5 LC; RelyX Veneer Cement; and Vario-link Esthetic LC). The volume loss ranged from 0.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!