Objectives: The purpose of this study was to compare the flexural strength and modulus of two commercial resin composites, at room temperature and 40, 45 and 50 degrees C prior to light polymerization with standard and step-cure protocols.
Methods: One nanohybrid (Grandio, VOCO, Cuxhaven, Germany), and microhybrid composite resin (Filtek Z250, 3M ESPE, St. Paul, MN, USA) were used. The materials were inserted into rectangular moulds at room temperature or preheated to a temperature of 40, 45 or 50 degrees C and cured with standard or step-cure protocols with high intensity halogen (Elipar Highlight, 3M-ESPE, St. Paul, MN, USA). Ten specimens were prepared for each preheating and light curing protocol. A three-point bending test was performed using a universal testing machine at a crosshead speed of 1 mm/min. The data were analyzed by one-way analysis of variance and Tukey's post hoc tests (P<.05) to examine the effect of curing protocol and preheating. Pearson's correlation test was used to determine the correlation between tested mechanical properties and preheating.
Results: There were no statistically significant difference between tested mechanical properties of the materials, curing protocols and temperature of the materials. No significant correlation was found between preheating and tested mechanical properties.
Conclusions: The mechanical properties of the tested materials did not changed by preheating so the tested materials could be preheated because of the other potential clinical advantages like more adaptation to the cavity walls.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC2634780 | PMC |
Publication Analysis
Top Keywords
Similar Publications
Clinical evaluation of single bond universal adhesive in non-carious cervical lesions: a 36-month retrospective study.
Clin Oral Investig
December 2024
Faculty of Dentistry, Department of Restorative Dentistry, Eskisehir Osmangazi University, Eskisehir, Turkey.
Objective: To evaluate the 36-month clinical performance of Single Bond Universal Adhesive (SBU; 3M ESPE, Germany) in non-carious cervical lesions (NCCLs) using different modes of adhesion according to the FDI criteria. The primary outcome was the retention loss of the restorations, while the secondary outcomes included marginal staining, marginal adaptation, post-operative sensitivity and tooth vitality, recurrence of caries erosion and abfraction, and tooth integrity, all evaluated according to the FDI criteria.
Materials And Methods: In this study, the SBU Adhesive was applied to 246 NCCLs of 25 patients using different modes of adhesion: Self-etch (SE), selective-enamel-etching (SLE), and etch-and-rinse (ER).
Translucency and contrast ratio of dimetharcyrlate resin based dental materials after bleaching: an in-vitro study.
BMC Oral Health
December 2024
Department of Restorative Dentistry, Faculty of Dentistry, Bolu Abant Izzet Baysal University, Bolu, Turkey.
Objective: To compare the translucency and contrast ratio of 13 different resin based restorative materials and to evaluate the effect of 2 different bleaching methods on the translucency and contrast ratio of these materials.
Methods: In this study, a total of 260 samples were prepared, 20 from each of 13 different dimethacrylate-based restorative materials. Then, each material group was divided into 4 subgroups.
Unveiling the mechanical performance of partially replaced coronal restorations in root canal-treated teeth: an in-vitro study.
BMC Oral Health
December 2024
Department of Conservative Dentistry, Faculty of Dentistry, Minia University, Minia, Egypt.
Objectives: To compare the mechanical performance of partially replaced (repaired) intra-coronal restorations to totally replaced ones in root canal-treated teeth.
Methods: Thirty maxillary second premolars were selected according to strict criteria, mounted on moulds, and had mesio-occluso-distal (MOD) cavities prepared. Resin composite restorative material was used to perform the initial restoration, followed by aging procedures using thermo-mechanical cycling fatigue to replicate six months of intraoral aging.
A technique to enhance the gingival esthetics of a prototype complete arch fixed implant-supported prototype prosthesis using a 3D printed gingival veneer.
J Prosthet Dent
December 2024
Clinical Professor and Program Director, University of Connecticut Health Center, Farmington, Conn.; and Private practice, Glastonbury, Conn. Electronic address:
An important step in the workflow for a complete arch fixed implant-supported prosthesis is the fabrication of a prototype resin prosthesis to allow the patient to visualize the definitive treatment outcome and also to use as an interim prosthesis. Producing a prototype prosthesis with the natural appearance of the gingival color and contour has been challenging. Current methods include painted stains, manually applied pink composite resin or autopolymerizing acrylic resin, and multicolored resin blocks, but these are all relatively expensive, have less than optimal esthetics, and are labor-intensive and time-consuming.
View Article and Find Full Text PDFCharacterization of a biocomposite film using coconut jelly powder to improve arrowroot starch and sodium alginate film forming properties.
Int J Biol Macromol
December 2024
Department of Marine, Faculty of Fisheries and Marine, Universitas Airlangga, Campus C UNAIR, Mulyorejo, Surabaya 60115, Indonesia; Research Group of Post-harvest, Processing Technology, and Bioproducts, Faculty of Fisheries and Marine, Universitas Airlangga, Mulyorejo, Surabaya 60115, Indonesia. Electronic address:
Composite polymers are promising solution to structural setbacks of starch and alginate-based films due to their hydrophilic attributes. Hence, this study aimed to investigate young coconut jelly powder (CJP), an under-utilized by-waste, as a filler using the casting method to develop a novel biocomposite from increments of CJP (1-3 %) to a blended resin of arrowroot starch, sodium alginate, and glycerol. Moreover, the films were characterized by physicomechanical (visual aspect, thickness, color, moisture content, tensile strength, and elongation at break); surface microstructure; water barrier (water vapor permeability, water solubility, and water activities); thermal, crystallinity, and functional group properties; soil, river water, and seawater biodegradability; and coating application in cherry tomato.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!