Thermoluminescence properties of undoped and Dy3+ doped ZrO2 nanophosphor under beta-ray irradiation.

The thermoluminescence (TL) of undoped and Dy3+ doped ZrO2 nanocrystals under beta-ray irradiation is reported. The TL glow curves are the result of the overlapping of four TL peaks produced partly by the intrinsic defect of highly asymmetrical monoclinic structure and partly due to defects produced during the synthesis process. The introduction of dopant ions induces changes in the glow curve due to the enhancement of high temperature peaks intensity. The results show that both undoped and doped ZrO2 nanocrystalline phosphor present good TL efficiency as well as good dose response which qualify them as a potential beta-ray dosimeter.