New vis active photocatalyst was obtained by the modification of commercial anatase TiO2 (Police, Poland) in pressure reactor in an ammonia water atmosphere at 100 degrees C for 4h. The photocatalytic activity of new material was tested during three azo dyes decomposition: monoazo (Reactive Read), diazo (Reactive Black) and poliazodye (Direct Green). Obtained photocatalyst had new bands at 1430-1440 cm(-1) attributed to the bending vibrations of NH(4)(+) and at 1535 cm(-1) associated with NH(2) groups or NO(2) and NO. UV-vis/DR spectra of photocatalyst had also insignificant decrease in visible region. Fluorescence technique was used for studying the amount of hydroxyl radicals produced on TiO2 surface during visible light irradiation. The hydroxyl radicals produced react with coumarin present in the solution to form 7-hydroxycoumarin which has fluorescent capacity. Photocatalytic activity of modified TiO2 was compared with commercial titanium dioxide P25 (Degussa, Germany). The photocatalytic activity of TiO2/N was higher than that of unmodified material and P25 under visible light irradiation. The ability for dye adsorption (Reactive Red) on photocatalyst surface was also tested. Unmodified TiO2 and P25 has isotherm of adsorption by Freundlich model, and nitrogen-modified TiO2 by Langmuir model. The presence of nitrogen at the surface of TiO2 significantly increased adsorption capacity of TiO2 as well as OH radicals formation under visible radiation.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.jhazmat.2008.11.024 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Synergistic Enhancement of Ligand & Cluster Connectivity to Construct Highly Stable Fluorescein-Based MOFs with Thickened Channel Walls for Boosting Photocatalytic Activity.
Small
January 2025
Jiangsu Key Laboratory of Green Synthetic Chemistry for Functional Materials, School of Chemistry and Materials Science, Jiangsu Normal, University Xuzhou, Jiangsu, 221116, P. R. China.
Fabricating visible-light-responsive metal-organic frameworks (MOFs) with high stability and effective catalytic functionality remains a long-term pursuit yet a great challenge. Herein, a strategy of increasing ligand and cluster connectivity is developed to construct highly stable fluorescein MOFs, La-CFL, presenting a new (4,8)-connected topological structure compared to Cd-FL constructed using 6-connected dinuclear clusters and 3-connected tritopic ligands. La(CFL) containers like Chinese "Ritual Wine Vessels (Jue)" resemble linear arrangements interconnected by the [La(COO)] clusters.
View Article and Find Full Text PDFSolar-Active Carbon Nitride Film Integrated by Free Radical Copolymerization for Photocatalytic Indoor Air Purification.
Small
January 2025
Department of Civil and Environment Engineering, University of Ulsan, Daehakro 93, Namgu, Ulsan, 44610, Republic of Korea.
The current lack of stable, scalable, and efficient coating technology dramatically limits the exploitation of solar-driven graphitic carbon nitride (CN) photocatalysts. Herein, a unique, efficient, and scalable method is reported to immobilize CN powder on various substrates ranging from Fluorine tin oxide (FTO), glass, Plexiglas, Al foil, Ti foil, and Granite stone, to even wood. The film shows an outstanding thickness of 212 µm, which is the highest value ever reported.
View Article and Find Full Text PDFEngineering Planar Crystallinity in Nitrogen-Vacancy-Incorporated Carbon Nitride for Efficient Photoredox Catalysis.
ACS Appl Mater Interfaces
January 2025
Key Laboratory of Functional Inorganic Material Chemistry, Ministry of Education of the People's Republic of China, School of Chemistry and Materials Science, Heilongjiang University, Harbin 150080, People's Republic of China.
The concurrent evolution of value-added benzimidazole compounds and hydrogen within the domain of chemical synthesis is of paramount importance. The utilization of photocatalysis enhances both the efficiency and environmental benignity of the synthetic process. However, it is profoundly challenging within a photocatalytic system to simultaneously augment the number of active sites and the internal transport rate of photogenerated charge carriers.
View Article and Find Full Text PDFPhotogenerated charge carrier dynamics on Pt-loaded SrTiO nanoparticles studied transient-absorption spectroscopy.
Nanoscale
January 2025
Research Center for Materials Nanoarchitectonics (MANA), National Institute for Materials Science (NIMS), 1-1 Namiki, Tsukuba, Ibaraki 305-0044, Japan.
Loading cocatalysts on semiconductor-based photocatalysts to create active reaction sites is a preferable method to enhance photocatalytic activity and a widely adopted strategy to achieve effective photocatalytic applications. Although theoretical calculations suggest that the broad density of states of noble metal cocatalysts, such as Pt, act as a recombination center, this has never been experimentally demonstrated. Herein, we employed pico-nano and nano-micro second transient absorption spectroscopy to investigate the often overlooked photogenerated holes, instead of the widely studied electrons on Pt- and Ni-loaded SrTiO to evaluate the effects of cocatalysts as a recombination center.
View Article and Find Full Text PDFPhotocatalytic degradation performance of a chitosan/ZnO-FeO nanocomposite over cationic and anionic dyes under visible-light irradiation.
RSC Adv
January 2025
Institute of Sciences and Technology, TNU-University of Sciences Thai Nguyen 250000 Vietnam
The sonochemical synthesis of a chitosan-ZnO/FeO nanocomposite yielded a highly porous structure and large surface area for enhancing the photocatalytic degradation of cationic (rhodamine B, RhB) and anionic (methyl orange, MO) dyes in aqueous solution. Chitosan-ZnO/FeO demonstrated a significant enhancement in photodegradation efficiency 99.49% for MO ( = 5.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!