Statement Of Problem: The wear resistance of nanofilled composite resin and feldspathic ceramic artificial teeth may vary according to the material type and physical characteristics of the antagonist.
Purpose: The purpose of this study was to evaluate the wear resistance of nanofilled composite resin and feldspathic ceramic artificial teeth after simulated mastication against steatite, zirconia, and alumina antagonists.
Material And Methods: The study evaluated 6 groups of artificial teeth: 3 groups of 8 nanofilled composite resin teeth (Condyloform II NFC) and 3 groups of 8 feldspathic ceramic teeth (Bonartic CT). Three sets of 16 steatite, 16 zirconia, and 16 alumina cusp-shaped antagonist surfaces were fabricated and used to test wear resistance. Each group was loaded for 600,000 cycles. The wear resistance was analyzed by measuring vertical and volume substance lost (microm and mm(3), respectively), determined with a laser scanner. Data were statistically analyzed using 2-way ANOVA and Games-Howell test (alpha=.05).
Results: The influence of the materials tested and antagonists was statistically significant. The composite resin teeth showed significantly higher vertical and volume substance loss than ceramic teeth opposing steatite cusps (P<.001; P=.04, respectively), while composite resin teeth opposing alumina and zirconia cusps demonstrated less wear than ceramic teeth. However, the latter differences were not statistically significant.
Conclusions: The wear behavior of nanofilled composite resin and feldspathic ceramic teeth varies according to the type of antagonistic material. However, alumina and zirconia ceramics caused less wear in antagonists than steatite ceramic.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/S0022-3913(08)60262-0 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Introducing PES porous membrane to establish bionic autocrine channels: A lubricating, anti-wear antifouling coating.
Mar Pollut Bull
January 2025
Department of Materials Science and Engineering, Dalian Maritime University, Dalian 116026, PR China; Dalian Key Laboratory of Internal Combustion Engine Tribology and Reliability Engineering, Dalian 116026, PR China. Electronic address:
As a global challenge, marine biofouling is causing serious economic losses and adverse ecological impacts. In recent years, a variety of promising and environmentally friendly anti-fouling strategies have emerged, among which the excellent anti-fouling performance of bionic autocrine coatings has been recognized. However, bionic autocrine coatings still suffer from uncontrollable secretion behavior, poor mechanical stability, and poor abrasion resistance.
View Article and Find Full Text PDFOptimization of surface roughness for titanium alloy based on multi-strategy fusion snake algorithm.
PLoS One
January 2025
School of Mechanical Engineering, Liaoning Technical University, Fuxin, China.
Titanium alloy is known for its low thermal conductivity, small elastic modulus, and propensity for work hardening, posing challenges in predicting surface quality post high-speed milling. Since surface quality significantly influences wear resistance, fatigue strength, and corrosion resistance of parts, optimizing milling parameters becomes crucial for enhancing service performance. This paper proposes a milling parameter optimization method utilizing the snake algorithm with multi-strategy fusion to improve surface quality.
View Article and Find Full Text PDFPhysicochemical Properties of Curen® Filaments Versus Nylon Filaments in Toothbrush Bristles: An In Vitro Study.
Cureus
December 2024
Medical Affairs, Dr. Reddy's Laboratories Ltd., Hyderabad, IND.
Background Toothbrush manufacturers commonly use bristle materials such as nylon, polybutylene terephthalate, polypropylene, polyethylene terephthalate, boar hair, bamboo, carbon fiber, silicone, polylactic acid, or their modifications such as Curen. Nylon filaments have long been demonstrated to be durable and are widely used, but not much is known regarding the performance of Curen filaments compared to nylon filaments. This in vitro study compared the stiffness, abrasion potential, abrasion resistance, and bristle surface changes of Curen and nylon filaments.
View Article and Find Full Text PDFCompressing slippery surface-assembled amphiphiles for tunable haptic energy harvesters.
Sci Adv
January 2025
Department of Chemical and Biomolecular Engineering, North Carolina State University, Raleigh, NC, USA.
A recurring challenge in extracting energy from ambient motion is that devices must maintain high harvesting efficiency and a positive user experience when the interface is undergoing dynamic compression. We show that small amphiphiles can be used to tune friction, haptics, and triboelectric properties by assembling into specific conformations on the surfaces of materials. Molecules that form multiple slip planes under pressure, especially through π-π stacking, produce 80 to 90% lower friction than those that form disordered mesostructures.
View Article and Find Full Text PDFIsolated Tin Enhanced CO Coverage-Regulation on SnCu Alloy for Selective CO Electroreduction to C Products.
Small
January 2025
Institute of Advanced Wear & Corrosion Resistant and Functional Materials, Jinan University, Guangzhou, 510632, P. R. China.
Electricity-powered C─C coupling of CO represents an attractive strategy for producing valuable commodity chemicals with renewable energy, but it is still challenging to gain high C selectivity at high current density. Here, a SnCu single-atom alloy (SAA) is reported with isolated Sn atom embedded into the Cu lattice, as efficient ectrocatalyst for CO reduction. The as prepared SnCu-SAA catalyst shows a maximal C Faradaic efficiency of 79.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!