This study examined the effects on the bond durability of resins arising from the application of adhesive agent on porcelain surface, silanated by a ceramic primer consisting of gamma-methacryloxypropyltrimethoxysilane (gamma-MPTS), by comparing shear bond strengths before and after thermocycling. When an adhesive agent was applied to a porcelain surface which had been silanated by a ceramic primer for 10 seconds, a significant reduction in resin bonding durability was observed. Extending the silanating period of the ceramic primer to 60 minutes resulted in an increase in resin bonding durability to the porcelain surface. However, the effect on resin bonding durability resulting from the application of adhesive agent was nearly the same as that without adhesive agent application, even though the porcelain surface was silanated for 60 minutes. In other words, positive effects arising from adhesive agent application on resin bonding durability were not observed.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.4012/dmj.27.427 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The effect of different adhesive strategies and diamond burs on dentin bond strength of universal resin cements.
Clin Oral Investig
January 2025
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo, Japan.
Objectives: To evaluate the shear bond strength (SBS) of universal cements (UCs) to dentin prepared with different diamond burs using various adhesive strategies.
Materials And Methods: One-hundred-twenty molars were prepared to expose the mid-coronal dentin. The teeth were divided into two groups according to diamond bur preparations: coarse and super-fine grit burs.
Determination of streptococcus mutans retention in acidic and neutral pH artificial saliva environment of all-ceramic materials with different surface treatment.
BMC Oral Health
January 2025
Department of Basic Medical Science, Faculty of Medicine, Yozgat Bozok University, Yozgat, 66100, Türkiye, Turkey.
Background: Although surface finishing processes are effective against Streptococcus mutans biofilm, the mechanism of action of saliva with different acidity values has not been studied in detail. This study aims to produce four different all-ceramic materials in a single session with CAD/CAM devices and apply two different surface finishing processes, glazing and polishing, and then determine the retention of Streptococcus mutants on the surfaces of the materials in saliva with varying levels of acidity.
Methods: Zirconia-reinforced lithium silicate (Vita Suprinity, Vita Zahnfabrik, Bad Saöckingen, Germany), monochromatic feldspar (Vitablocs Mark 2, Vita Zahnfabrik, Bad Saöckingen, Germany), leucite glass ceramic (IPS Empress CAD, Ivoclar Vivadent, Liechtenstein), and monolithic zirconia (Incoris TZI (Cerec) Sirona, Germany) were used in the study.
Shear bond strength and ARI scores of metal brackets to glazed glass ceramics and zirconia: an in vitro study investigating surface treatment protocols.
BMC Oral Health
December 2024
Faculty of Dentistry, Innovative Dental Materials and Interfaces Research Unit (URB2i), UR 4462, Paris Cité University, 1 rue Maurice Arnoux, Montrouge, 92120, France.
Objective: To evaluate the shear bond strength (SBS) and adhesive remnant index (ARI) scores of metal brackets to glazed lithium disilicate reinforced glass-ceramics and zirconia according to various surface treatment protocols.
Methods: A total of 240 lithium disilicate ceramic (LD) and 240 zirconia (Zr) blocks were randomly divided according to sandblasting, hydrofluoric acid (HF) etching, universal primer use, and the adhesive system applied. A maxillary canine metal bracket was bonded to each sample with resin cement (Transbond XT, TXT).
Evaluating fatigue resistance in occlusal veneers: a comparative study of processing techniques and material thickness of lithium disilicate (IPS e.max Press vs. IPS e.max CAD).
BMC Oral Health
December 2024
Department of Prosthodontics, Faculty of Dentistry, Chiang Mai University, Chiang Mai, Thailand.
Background: Lithium disilicate occlusal veneers are popular for minimally invasive posterior teeth restoration. The aim of this study was to compare the fatigue resistance and crack pattern of lithium disilicate occlusal veneers fabricated using pressing and milling techniques with varying thicknesses.
Methods: Sixty lithium disilicate discs, representing occlusal veneers, were divided into four groups (n = 15) based on processing technique (IPS e.
Purpose: The purpose of this laboratory study was to evaluate common materials for isolation and neutralizing agents for hydrofluoric acid (HF). Additionally, surfaces of lithium disilicate ceramic were examined for precipitates after the etching and neutralizing process.
Materials And Methods: The HF permeability of the following isolation agents (n=8) was investigated by positioning them over pH indicator paper under airtight conditions and applying 9% HF: latex rubber dam; elastic plastomer rubber dam; nitrile gloves; latex gloves; liquid rubber dam; Teflon; AZ strip.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!